Characterization of mechano-thermally synthesized Curie temperature-adjusted La{sub 0.8}Sr{sub 0.2}MnO{sub 3} nanoparticles coated with (3-aminopropyl) triethoxysilane

Journal Article · Sat Aug 15 00:00:00 EDT 2015 · Materials Characterization

DOI:https://doi.org/10.1016/J.MATCHAR.2015.05.025· OSTI ID:22476124

Salili, S. M. ^[1]; Barati, M. R. ^[2]; Sadighi, Z. ^[2]

---

1. Chemical Physics Interdisciplinary Program, Liquid Crystal Institute, Kent State University, Kent, OH 44242 (United States)
2. School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran (Iran, Islamic Republic of)

This research aimed to synthesize nanostructured strontium-doped lanthanum manganite, La{sub 0.8}Sr{sub 0.2}MnO{sub 3} (LSMO), with its Curie temperature (T{sub c}) adjusted to the therapeutic range, through a mechanothermal route. In order to investigate the effect of heat treatment temperature and duration on the resulting crystallite size, morphology, magnetic behavior and Curie temperature, the starting powder mixture was milled in a planetary ball mill before being subsequently heat treated at distinct temperatures for different time lengths. The composition, morphology, and magnetic behavior were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED) and vibrating sample magnetometer (VSM). In addition, magnetic properties were further investigated using an alternating current (AC) susceptometer and thermo-magnetic analyzer. 20 h of milling produced a crystallite size reduction leading to a decrease in the heat treatment temperature of LSMO synthesis to 800 °C. Moreover, SEM analysis has shown the morphology of a strong agglomeration of fine nanoparticles. HRTEM showed clear lattice fringes of high crystallinity. The mean crystallite and particle size of 20-hour milled sample heat treated at 1100 °C for 10 h are relatively 69 and 100 nm, respectively. The VSM data at room temperature, indicated a paramagnetic behavior for samples heat treated at 800 °C. However, by increasing heat treatment temperature to 1100 °C, LSMO indicates a ferromagnetic behavior with well-adjusted Curie temperature of 320 K, suitable for hyperthermia applications. Also, reentrant spin glass (RSG) behavior has been found in heat treated samples. The particles are coated with (3-aminopropyl) triethoxysilane (APTES) for biocompatibility purposes; Fourier transform infrared spectroscopy (FTIR) and thermo-gravimetric analysis (TGA) are used for further confirmation of APTES coating. - Highlights: • La{sub 0.8}Sr{sub 0.2}MnO{sub 3} nanoparticles were synthesized via a mechanothermal route. • We report a significant reduction in the heat treatment temperature. • The Curie temperature was tuned within the therapeutic range. • The particles were coated with (3-aminopropyl) triethoxysilane for biocompatibility purposes.

• OSTI ID: 22476124
• Journal Information: Materials Characterization, Vol. 106; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
• Country of Publication: United States
• Language: English

Related Subjects

77 NANOSCIENCE AND NANOTECHNOLOGY
CURIE POINT
DOPED MATERIALS
ELECTRON DIFFRACTION
FOURIER TRANSFORM SPECTROMETERS
HEAT TREATMENTS
INFRARED SPECTRA
LANTHANUM COMPOUNDS
MAGNETIC ANALYZERS
MAGNETIC PROPERTIES
MANGANATES
NANOPARTICLES
NANOSTRUCTURES
PARAMAGNETISM
SCANNING ELECTRON MICROSCOPY
SPIN GLASS STATE
STRONTIUM COMPOUNDS
THERMAL GRAVIMETRIC ANALYSIS
TRANSMISSION ELECTRON MICROSCOPY
VIBRATING SAMPLE MAGNETOMETERS
X-RAY DIFFRACTION