Syntheses, structures, and ionic conductivities of perovskite-structured lithium–strontium–aluminum/gallium–tantalum-oxides
- Department of Electronic Chemistry, Interdisciplinary Graduate School of Science and Engineering, Tokyo Institute of Technology, 4259 Nagatsuta, Midori, Yokohama 226-8502 (Japan)
- Department of Chemistry, Mie University, 1577 Kurimamachiyacho, Tsu, Mie 514-8507 (Japan)
- High Energy Accelerator Research Organization, Tokai-mura, Naka-gun, Ibaraki 319-1106 (Japan)
The ionic conductivities of new perovskite-structured lithium–strontium–aluminum/gallium–tantalum oxides were investigated. Solid solutions of the new perovskite oxides, (Li{sub x}Sr{sub 1−x})(Al{sub (1−x)/2}Ta{sub (1+x)/2})O{sub 3} and (Li{sub x}Sr{sub 1−x})(Ga{sub (1−x)/2}Ta{sub (1+x)/2})O{sub 3}, were synthesized using a ball-milled-assisted solid-state method. The partial substitution of the smaller Ga{sup +3} for Ta{sup +5} resulted in new compositions, the structures of which were determined by neutron diffraction measurements using a cubic perovskite structural model with the Pm−3m space group. Vacancies were introduced into the Sr(Li) sites by the formation of solid solutions with compositions (Li{sub x}Sr{sub 1−x−y}☐{sub y})(Ga{sub [(1−x)/2]−y}Ta{sub [(1+x)/2]+y})O{sub 3}, where the composition range of 0≤y≤0.20 was examined for x=0.2 and 0.25. The highest conductivity, 1.85×10{sup −3} S cm{sup −1} at 250 °C, was obtained for (Li{sub 0.25}Sr{sub 0.625}☐{sub 0.125})(Ga{sub 0.25}Ta{sub 0.75})O{sub 3} (x=0.25, y=0.125). Enhanced ionic conductivities were achieved by the introduction of vacancies at the A-sites. - Graphical abstract: Novel lithium-conducting oxides with the cubic perovskite structure (Li{sub x}Sr{sub 1−x−y}☐{sub y})(Ga{sub [(1−x)/2]−y}Ta{sub [(1+x)/2]+y})O{sub 3} provide a specific solid-solution region with various x and y values, exhibiting the highest ionic conductivity (1.85 S cm{sup −1} at 250 °C) for (Li{sub 0.25}Sr{sub 0.625}☐{sub 0.125})(Ga{sub 0.25}Ta{sub 0.75})O{sub 3} (x=0.25, y=0.125 in (Li{sub x}Sr{sub 1−x−y}☐{sub y})(Ga{sub [(1−x)/2]−y}Ta{sub [(1+x)/2]+y})O{sub 3}). The vacancies (☐) introduced into the A-sites contribute to the enhancement of lithium diffusion in the perovskite structure because of the enlargement of the bottleneck size and suppression of the interaction between lithium and oxygen. - Highlights: • The perovskite-structured novel Li–Sr–Al/Ga–Ta oxides were investigated. • The Ga cation offers a larger bottleneck by increasing the B−O bond length. • The greater conductivity was observed upon Ga-containing perovskite. • The ionic conductivity was improved by the introduction of vacancies into A-site.
- OSTI ID:
- 22475625
- Journal Information:
- Journal of Solid State Chemistry, Vol. 225; Other Information: Copyright (c) 2015 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigation into the effect of Si doping on the cell symmetry and performance of Sr{sub 1−y}Ca{sub y}FeO{sub 3−δ} SOFC cathode materials
Amorphous and crystalline alkali ion conductors
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ALUMINIUM COMPOUNDS
BOND LENGTHS
CATIONS
DIFFUSION
GALLIUM COMPOUNDS
GALLIUM IONS
IONIC CONDUCTIVITY
LITHIUM COMPOUNDS
NEUTRON DIFFRACTION
OXYGEN
SOLID ELECTROLYTES
SOLID SOLUTIONS
STRONTIUM COMPOUNDS
STRUCTURAL MODELS
SYNTHESIS
TANTALUM IONS
TANTALUM OXIDES
VACANCIES