Influence of magnesia-to-phosphate molar ratio on microstructures, mechanical properties and thermal conductivity of magnesium potassium phosphate cement paste with large water-to-solid ratio
- Department of Civil and Environmental Engineering, The Hong Kong University of Science and Technology, Clear Water Bay, Kowloon, Hong Kong (China)
This paper describes the influence of the magnesia-to-phosphate (M/P) molar ratios ranging from 4 to 12, on the properties and microstructures of magnesium potassium phosphate cement (MKPC) pastes with a large water-to-solid ratio (w/s) of 0.50. The setting behavior, compressive strength, tensile bonding strength and thermal conductivity of the MKPC pastes, were investigated. The results show that an increase in the M/P ratio can slow down the setting reaction, and clearly degrade the mechanical strengths, but clearly improve the thermal conductivity of MKPC pastes. Furthermore, micro-characterizations including X-ray diffraction, scanning electron microscopy and thermogravimetric analysis, on the MKPC pastes reveal that a lower M/P ratio can facilitate better crystallization of the resultant magnesium potassium phosphate hexahydrate (MKP) and a denser microstructure. Moreover, strong linear correlations are found between the mechanical strengths and the MKP-to-space ratio, and between thermal conductivity and the volume ratio of the unreacted magnesia to the MKP. - Highlights: • Increase of M/P molar ratio causes clear mechanical degradations on MKPC pastes. • Thermal conductivity of MKPC pastes is improved with increase of M/P molar ratio. • Lower M/P ratio leads to better MKP crystallization and denser microstructure. • Strengths of MKPC pastes are linearly correlated to the MKP-to-space ratios. • Thermal conductivity is affected by the volume ratio of unreacted magnesia to MKP.
- OSTI ID:
- 22475481
- Journal Information:
- Cement and Concrete Research, Vol. 68; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0008-8846
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reaction mechanism of magnesium potassium phosphate cement with high magnesium-to-phosphate ratio
Influence of fly ash and metakaolin on the microstructure and compressive strength of magnesium potassium phosphate cement paste