Transformation of dense AgI into a silver-rich framework iodide using thiophenol as mineralizer
A new three-dimensional framework iodide, (DabcoH){sub 2}[(Dabco){sub 2}Ag{sub 14}I{sub 16}] (1), was solvothermal synthesized by transformation of dense AgI using p-methylthiophenol as mineralizer, and characterized by elemental analysis, single-crystal and powder X-ray diffraction, thermogravimetric analysis, differential scanning calorimetry analysis, UV–vis diffuse reflectance spectroscopy and fluorescence spectroscopy. Compound 1 crystallizes in the trigonal space group R-3c, a=13.4452(2) Å, c=63.725(2) Å, V=9976.5(4) Å{sup 3}, Z=6. It features a 3D silver-rich [(Dabco){sub 2}Ag{sub 14}I{sub 16}]{sup 2−} anionic framework built up from corner-sharing of hybrid [(Dabco){sub 2}Ag{sub 14}I{sub 19}]{sup 5−} clusters, with protonated DabcoH{sup +} as counterions residing in the channels. UV–vis reflectance spectroscopy reveals the band gap of 1 is 3.3 eV. Compound 1 exhibits a strong photoluminescent emission band at 567 nm upon excitation at 489 nm. - Graphical abstract: A new 3-D iodoargentate was synthesized by transformation of dense AgI in I{sup −}-deficient system using thiophenol as mineralizer. - Highlights: • We have developed a new method to synthesize iodide using thiophenol as mineralizer. • A new 3D iodide, (DabcoH){sub 2}[(Dabco){sub 2}Ag{sub 14}I{sub 16}], was synthesized by transformation of dense AgI under solvothermal condition. • The compound features a 3D Ag–I framework with highest Ag/I ratio. • Compound 1 is a semiconductor with the band gap of 3.3 eV. • Compound 1 exhibits a strong photoluminescent emission band at 567 nm upon excitation at 489 nm.
- OSTI ID:
- 22451129
- Journal Information:
- Journal of Solid State Chemistry, Vol. 220; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis, structure and characterization of two new open-framework gallium phosphite-oxalates of varying dimensionality
Calcio-olivine {gamma}-Ca{sub 2}SiO{sub 4}: I. Rietveld refinement of the crystal structure