Effect of Cu addition on the martensitic transformation of powder metallurgy processed Ti–Ni alloys
- Department of Advanced Materials Engineering, Keimyung University, 1000 Shindang-dong Dalseo-gu, Daegu 704-701 (Korea, Republic of)
- Department of Civil Engineering, Hongik University, 72-1 Sangsu-dong Mapo-gu, Seoul 121-791 (Korea, Republic of)
Highlights: • M{sub s} of Ti{sub 50}Ni{sub 50} powders is 22 °C, while M{sub s} of SPS-sintered porous bulk increases up to 50 °C. • M{sub s} of Ti{sub 50}Ni{sub 40}Cu{sub 20} porous bulk is only 2 °C higher than that of the powders. • Recovered stain of porous TiNi and TiNiCu alloy is more than 1.5%. - Abstract: Ti{sub 50}Ni{sub 50} and Ti{sub 50}Ni{sub 30}Cu{sub 20} powders were prepared by gas atomization and their transformation behaviors were examined by means of differential scanning calorimetry and X-ray diffraction. One-step B2–B19’ transformation occurred in Ti{sub 50}Ni{sub 50} powders, while Ti{sub 50}Ni{sub 30}Cu{sub 20} powders showed B2–B19 transformation behavior. Porous bulks with 24% porosity were fabricated by spark plasma sintering. The martensitic transformation start temperature (50 °C) of Ti{sub 50}Ni{sub 50} porous bulk is much higher than that (22 °C) of the as-solidified powders. However, the martensitic transformation start temperature (35 °C) of Ti{sub 50}Ni{sub 30}Cu{sub 20} porous bulk is almost the same as that (33 °C) of the powders. When the specimens were compressed to the strain of 8% and then unloaded, the residual strains of Ti{sub 50}Ni{sub 50} and Ti{sub 50}Ni{sub 30}Cu{sub 20} alloy bulks were 3.95 and 3.7%, respectively. However, these residual strains were recovered up to 1.7% after heating by the shape memory phenomenon.
- OSTI ID:
- 22420598
- Journal Information:
- Materials Research Bulletin, Vol. 58; Conference: IFFM2013: International forum on functional materials, Jeju City (Korea, Republic of), 27-29 Jun 2013; Other Information: Copyright (c) 2014 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of stress on the transformation in nickel-titanium
Microstructure and martensitic transformation in Si-coated TiNi powders prepared by ball milling