Strategy for stabilization of the antiferroelectric phase (Pbma) over the metastable ferroelectric phase (P2{sub 1}ma) to establish double loop hysteresis in lead-free (1−x)NaNbO{sub 3}-xSrZrO{sub 3} solid solution
- Materials Research Institute, The Pennsylvania State University, University Park, Pennsylvania 16802 (United States)
- Taiyo Yuden Co., Ltd., Takasaki, Gunma 370-3347 (Japan)
A new lead-free antiferroelectric solid solution system, (1−x)NaNbO{sub 3}-xSrZrO{sub 3}, was rationalized through noting the crystal chemistry trend, of decreasing the tolerance factor and an increase in the average electronegativity of the system. The SrZrO{sub 3} doping was found to effectively stabilize the antiferroelectric (P) phase in NaNbO{sub 3} without changing its crystal symmetry. Preliminary electron diffraction and polarization measurements were presented which verified the enhanced antiferroelectricity. In view of our recent report of another lead-free antiferroelectric system (1−x)NaNbO{sub 3}-xCaZrO{sub 3} [H. Shimizu et al. “Lead-free antiferroelectric: xCaZrO{sub 3} - (1−x)NaNbO{sub 3} system (0 ≤ x ≤ 0.10),” Dalton Trans. (published online)], the present results point to a general strategy of utilizing tolerance factor to develop a broad family of new lead-free antiferroelectrics with double polarization hysteresis loops. We also speculate on a broad family of possible solid solutions that could be identified and tested for this important type of dielectric.
- OSTI ID:
- 22412871
- Journal Information:
- Journal of Applied Physics, Vol. 117, Issue 21; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural evolution in NaNbO{sub 3}-based antiferroelectrics
Direct evidence of an incommensurate phase in NaNbO{sub 3} and its implication in NaNbO{sub 3}-based lead-free antiferroelectrics