Effect of cooling rate on the properties of high density polyethylene/multi-walled carbon nanotube composites
- School of Mechanical and Aerospace Engineering, Queen’s University Belfast, BT9 5AH (United Kingdom)
- School of Electronics, Electrical Engineering and Computer Science, Queen’s University Belfast, BT9 5AH (United Kingdom)
High density polyethylene (HDPE)/multi-walled carbon nanotube (MWCNT) nanocomposites were prepared by melt mixing using twin-screw extrusion. The extruded pellets were compression moulded at 200°C for 5min followed by cooling at different cooling rates (20°C/min and 300°C/min respectively) to produce sheets for characterization. Scanning electron microscopy (SEM) shows that the MWCNTs are uniformly dispersed in the HDPE. At 4 wt% addition of MWCNTs composite modulus increased by over 110% compared with the unfilled HDPE (regardless of the cooling rate). The yield strength of both unfilled and filled HDPE decreased after rapid cooling by about 10% due to a lower crystallinity and imperfect crystallites. The electrical percolation threshold of composites, irrespective of the cooling rate, is between a MWCNT concentration of 1∼2 wt%. Interestingly, the electrical resistivity of the rapidly cooled composite with 2 wt% MWCNTs is lower than that of the slowly cooled composites with the same MWCNT loading. This may be due to the lower crystallinity and smaller crystallites facilitating the formation of conductive pathways. This result may have significant implications for both process control and the tailoring of electrical conductivity in the manufacture of conductive HDPE/MWCNT nanocomposites.
- OSTI ID:
- 22391858
- Journal Information:
- AIP Conference Proceedings, Vol. 1664, Issue 1; Conference: PPS-30: 30. International Conference of the Polymer Processing Society, Cleveland, OH (United States), 6-12 Jun 2014; Other Information: (c) 2015 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
A Comparative Study on AC Conductivity and Dielectric Behavior of Multiwalled Carbon Nanotubes and Polyaniline Coated Multiwalled Carbon Nanotubes Filled High Density Polyethylene-Carbon Black Nanocomposites
Effect of Multi-Walled Carbon Nanotubes on Viscoelastic Properties of PP/Reed Flour Composites