Fabrication and characterization of Cu(In,Ga)Se{sub 2} p-channel thin film transistors
- Graduate Institute of Electronics Engineering and Department of Electrical Engineering, National Taiwan University, Taipei, Taiwan (China)
Cu(In,Ga)Se{sub 2} thin film transistors are demonstrated with the on-off ratio of ∼10{sup 3} and the saturation hole mobility of 1.8 cm{sup 2}/V-s. Due to the high hole concentration (∼5 × 10{sup 17 }cm{sup −3}), the channel needs to be etched to turn off for the accumulation mode operation. The Cu(In,Ga)Se{sub 2} film after etching reveals a larger mobility, and a narrower (112) X-ray diffraction line than the original thick layer, indicating the better crystallinity of the initial growth as compared to the subsequent Cu(In,Ga)Se{sub 2} layer. Both the hole concentration and the saturation mobility increase with the decreasing Cu/(In + Ga) ratio probably due to the effect of Cu vacancies.
- OSTI ID:
- 22350865
- Journal Information:
- Applied Physics Letters, Vol. 105, Issue 14; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA); ISSN 0003-6951
- Country of Publication:
- United States
- Language:
- English
Similar Records
Air-Stable CuInSe2 Nanocrystal Transistors and Circuits via Post-Deposition Cation Exchange
High performance indium gallium zinc oxide thin film transistors fabricated on polyethylene terephthalate substrates
Structure and optoelectronic properties of single crystal epitaxial Cu(In{sub 1{minus}x}Ga{sub x})Se{sub 2} and ordered defect compounds
Journal Article
·
Fri Feb 01 00:00:00 EST 2019
· ACS Nano
·
OSTI ID:22350865
+7 more
High performance indium gallium zinc oxide thin film transistors fabricated on polyethylene terephthalate substrates
Journal Article
·
Mon Aug 25 00:00:00 EDT 2008
· Applied Physics Letters
·
OSTI ID:22350865
+5 more
Structure and optoelectronic properties of single crystal epitaxial Cu(In{sub 1{minus}x}Ga{sub x})Se{sub 2} and ordered defect compounds
Book
·
Sat Dec 31 00:00:00 EST 1994
·
OSTI ID:22350865
+2 more