Hydrostatic pressure (8 GPa) dependence of electrical resistivity of BaCo{sub 2}As{sub 2} single crystal
- Institute for Solid State Physics, The University of Tokyo, Kashiwanoha, Kashiwa, Chiba 277-8581 (Japan)
- Centre for High Pressure Research, School of Physics, Bharathidasan University, Tiruchirappalli 620024 (India)
Graphical abstract: - Highlights: • Single crystals of BaCo{sub 2}As{sub 2} were grown by CoAs self-flux method. • We have studied pressure effects (8 GPa) on dc electrical resistivity of BaCo{sub 2}As{sub 2}. • On applied external pressure BaCo{sub 2}As{sub 2} remains a metallic state up to 8 GPa. • Superconductivity is absent in BaCo{sub 2}As{sub 2} because of its proximity to ferromagnetism. - Abstract: The pressure dependence of the electrical resistivity of BaCo{sub 2}As{sub 2} single crystal as a function of temperature was measured at ambient and high pressures up to 8 GPa for the first time using cubic anvil high pressure cell. It is observed that at room temperature the resistivity monotonically decreases with increasing pressure and it remains in the metallic state even at an applied pressure of 8 GPa. From the temperature dependence of the resistivity measurements under pressure, we found that superconductivity is absent up to 8 GPa. The value of the electron's scattering factor (A) is found to be large at ambient pressure and it decreases with the application of pressure, indicating that the substantial electron correlation effect of BaCo{sub 2}As{sub 2} is reduced under pressure, revealing a dramatic change of density of states at the Fermi energy.
- OSTI ID:
- 22285163
- Journal Information:
- Materials Research Bulletin, Vol. 48, Issue 10; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 0025-5408
- Country of Publication:
- United States
- Language:
- English
Similar Records
Metastable phase of UTe2 formed under high pressure above 5 GPa
High-precision measurements of the compressibility and the electrical resistivity of bulk g-As{sub 2}Te{sub 3} glasses at a hydrostatic pressure up to 8.5 GPa