Title: Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution

Abstract

Crystals of Sr{sub 4−x}Ln{sub x}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} (x=0; x∼0.15 for Ln=La, Pr, Nd, Sm. Eu, Gd, Dy; x∼0.3 for Ln=Gd) were isolated upon using high-temperature, solid-state methods in molten-salt media. These compounds are isostructural with the previously reported Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3} (Ln=La, Sm, Gd) series that contains the same [MnO{sub 4}]{sub ∞} spin chains. The synthesis of the Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} (x=0) phase was carried out by a double aliovalent substitution with respect to the Sr{sup 2+} and Ge{sup 4+} ions that replace Na{sup +}/Ln{sup 3+} and As{sup 5+} in Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}, respectively. The title series contains mixed-valent Mn(III)/Mn(IV) and shows a limited range of solid solution, both of which were not observed in the previously reported Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3} series. To form the Sr{sub 4−x}Ln{sub x}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} solid solution, one of the Sr{sup 2+} sites, i.e., the original Ln-site in Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}, is partially substituted by Ln{sup 3+} in a statistical disorder of Sr{sub 1−x}/Ln{sub x}. Initial magnetic investigations of selected derivatives reveal higher ferromagnetic ordering temperatures than those reported for the Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){submore » 3} series, presumably attributed to a lesser degree of canting as a result of introducing non-Jahn–Teller Mn{sup 4+} ions. Also intriguing is the observation of multiple anomalies at low temperatures which appear to be of electronic origins. - Graphical abstract: Sr{sub 4−x}Ln{sub x}Mn(III){sub 2+x}Mn(IV){sub 1−x}O{sub 3}(GeO{sub 4}){sub 3}. Display Omitted - Highlights: • Double aliovalent substitution: Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} with respect to Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}. • Solid solution with respect to statistical disorder of Sr{sub 1−x}Ln{sub x} in one of the two Sr sites. • Mn{sup 3+}/Mn{sup 4+} magnetic ions are spatially arranged in a triangular kagomé fashion. • Enhanced ferromagnetic ordering attributed to doping non-Jahn–Teller Mn{sup 4+}.« less

Authors:
;  [1];  [2]; ;  [3];  [4];  [1]
  1. Department of Chemistry, Clemson University, Clemson, SC 29634 (United States)
  2. E. I. du Pont, Wilmington, DE 19880-0500 (United States)
  3. Department of Physics and Astronomy, Clemson University, Clemson, SC 29634 (United States)
  4. Wuhan University of Technology, Wuhan 430070 (China)
Publication Date:
OSTI Identifier:
22274104
Resource Type:
Journal Article
Resource Relation:
Journal Name: Journal of Solid State Chemistry; Journal Volume: 206; Other Information: Copyright (c) 2013 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 36 MATERIALS SCIENCE; ARSENATES; ARSENIC IONS; CRYSTALS; FERROMAGNETISM; GERMANIUM OXIDES; MANGANESE IONS; MOLTEN SALTS; PERMANGANATES; SODIUM IONS; SOLID SOLUTIONS; SOLIDS; SPIN; STRONTIUM IONS; SYNTHESIS

Citation Formats

West, J. Palmer, Sulejmanovic, Dino, Becht, Gregory, He, Jian, Hitchcock, Dale, Yan, Yonggao, and Hwu, Shiou-Jyh, E-mail: shwu@clemson.edu. Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution. United States: N. p., 2013. Web. doi:10.1016/J.JSSC.2013.07.033.
West, J. Palmer, Sulejmanovic, Dino, Becht, Gregory, He, Jian, Hitchcock, Dale, Yan, Yonggao, & Hwu, Shiou-Jyh, E-mail: shwu@clemson.edu. Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution. United States. doi:10.1016/J.JSSC.2013.07.033.
West, J. Palmer, Sulejmanovic, Dino, Becht, Gregory, He, Jian, Hitchcock, Dale, Yan, Yonggao, and Hwu, Shiou-Jyh, E-mail: shwu@clemson.edu. Tue . "Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution". United States. doi:10.1016/J.JSSC.2013.07.033.
@article{osti_22274104,
title = {Enhanced ferromagnetic order in Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} featuring canted [MnO{sub 4}]{sub ∞} spin chains of mixed-valent Mn(III)/Mn(IV). Aliovalent substitution of the Sr{sub 4−x}Ln{sub x}Mn{sup III}{sub 2+x}Mn{sup IV}{sub 1−x}O{sub 3}(GeO{sub 4}){sub 3} solid-solution},
author = {West, J. Palmer and Sulejmanovic, Dino and Becht, Gregory and He, Jian and Hitchcock, Dale and Yan, Yonggao and Hwu, Shiou-Jyh, E-mail: shwu@clemson.edu},
abstractNote = {Crystals of Sr{sub 4−x}Ln{sub x}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} (x=0; x∼0.15 for Ln=La, Pr, Nd, Sm. Eu, Gd, Dy; x∼0.3 for Ln=Gd) were isolated upon using high-temperature, solid-state methods in molten-salt media. These compounds are isostructural with the previously reported Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3} (Ln=La, Sm, Gd) series that contains the same [MnO{sub 4}]{sub ∞} spin chains. The synthesis of the Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} (x=0) phase was carried out by a double aliovalent substitution with respect to the Sr{sup 2+} and Ge{sup 4+} ions that replace Na{sup +}/Ln{sup 3+} and As{sup 5+} in Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}, respectively. The title series contains mixed-valent Mn(III)/Mn(IV) and shows a limited range of solid solution, both of which were not observed in the previously reported Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3} series. To form the Sr{sub 4−x}Ln{sub x}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} solid solution, one of the Sr{sup 2+} sites, i.e., the original Ln-site in Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}, is partially substituted by Ln{sup 3+} in a statistical disorder of Sr{sub 1−x}/Ln{sub x}. Initial magnetic investigations of selected derivatives reveal higher ferromagnetic ordering temperatures than those reported for the Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3} series, presumably attributed to a lesser degree of canting as a result of introducing non-Jahn–Teller Mn{sup 4+} ions. Also intriguing is the observation of multiple anomalies at low temperatures which appear to be of electronic origins. - Graphical abstract: Sr{sub 4−x}Ln{sub x}Mn(III){sub 2+x}Mn(IV){sub 1−x}O{sub 3}(GeO{sub 4}){sub 3}. Display Omitted - Highlights: • Double aliovalent substitution: Sr{sub 4}Mn{sub 3}O{sub 3}(GeO{sub 4}){sub 3} with respect to Na{sub 3}LnMn{sub 3}O{sub 3}(AsO{sub 4}){sub 3}. • Solid solution with respect to statistical disorder of Sr{sub 1−x}Ln{sub x} in one of the two Sr sites. • Mn{sup 3+}/Mn{sup 4+} magnetic ions are spatially arranged in a triangular kagomé fashion. • Enhanced ferromagnetic ordering attributed to doping non-Jahn–Teller Mn{sup 4+}.},
doi = {10.1016/J.JSSC.2013.07.033},
journal = {Journal of Solid State Chemistry},
number = ,
volume = 206,
place = {United States},
year = {Tue Oct 15 00:00:00 EDT 2013},
month = {Tue Oct 15 00:00:00 EDT 2013}
}