Interface conditions of two-shot molded parts
- Polymer Competence Center Leoben GmbH, 8700 Leoben (Austria)
- Department of Polymer Engineering and Science, Chair of Materials Science and Testing of Polymers, Montanuniversitaet Leoben, 8700 Leoben (Austria)
- Department of Polymer Engineering and Science, Chair of Polymer Processing, Montanuniversitaet Leoben, 8700 Leoben (Austria)
The focus of this work is on interfaces of two-shot molded parts. It is well known that e.g. material combination, process parameters and contact area structures show significant effects on the bond strength of multi-component injection molded parts. To get information about the bond strength at various process parameter settings and material combinations a test mold with core back technology was used to produce two-component injection molded tensile test specimens. At the core back process the different materials are injected consecutively, so each component runs through the whole injection molding cycle (two-shot process). Due to this consecutive injection molding processes, a cold interface is generated. This is defined as overmolding of a second melt to a solidified polymer preform. Strong interest lies in the way the interface conditions change during the adhesion formation between the individual components. Hence the interface conditions were investigated by computed tomography and Raman spectroscopy. By analyzing these conditions the understanding of the adhesion development during the multi-component injection molding was improved.
- OSTI ID:
- 22270971
- Journal Information:
- AIP Conference Proceedings, Vol. 1593, Issue 1; Conference: PPS-29: 29. international conference of the Polymer Processing Society, Nuremberg (Germany), 15-19 Jul 2013; Other Information: (c) 2014 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0094-243X
- Country of Publication:
- United States
- Language:
- English
Similar Records
Energy Reductions Using Next-Generation Remanufacturing Techniques
High-performance molded composites using additively manufactured preforms with controlled fiber and pore morphology