Title: Microstructural and optical studies on sonochemically synthesized Cu doped ZnO nanoparticles

Abstract

Copper doped ZnO nanoparticles were synthesized by sonochemical method varying the concentration of the impurity. Systematic investigations like X-ray diffraction (XRD) and Transmission electron microscopy (TEM) were carried out to understand the microstructural properties. The average particle sizes and all the crystallographic parameters were calculated from XRD results. This shows the formation of wurtzite phase of ZnO with average size of the particles as 53 nm and an increase of particle size with dopant concentration was also been observed. UV absorption and Fourier transformed infrared spectroscopy (FTIR) spectra revealed the absorption at wavelength < 370 nm with a remarkable red shift of absorption band and a linear decrease of transmittance with increase in doping concentrations respectively.

Authors:
; ;  [1];  [2]
  1. Sambalpur University, Jyoti Vihar, Burla -768019, Odisha (India)
  2. C.V. Raman College of Engineering, Bhubaneswar-752054, Odisha (India)
Publication Date:
OSTI Identifier:
22269439
Resource Type:
Journal Article
Resource Relation:
Journal Name: AIP Conference Proceedings; Journal Volume: 1591; Journal Issue: 1; Conference: 58. DAE solid state physics symposium 2013, Patiala, Punjab (India), 17-21 Dec 2013; Other Information: (c) 2014 AIP Publishing LLC; Country of input: International Atomic Energy Agency (IAEA)
Country of Publication:
United States
Language:
English
Subject:
37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; 77 NANOSCIENCE AND NANOTECHNOLOGY; ABSORPTION; COPPER; CRYSTALLOGRAPHY; DOPED MATERIALS; FOURIER TRANSFORM SPECTROMETERS; FOURIER TRANSFORMATION; IMPURITIES; INFRARED SPECTRA; MICROSTRUCTURE; NANOSTRUCTURES; PARTICLE SIZE; PARTICLES; SYNTHESIS; TRANSMISSION ELECTRON MICROSCOPY; X-RAY DIFFRACTION; ZINC OXIDES

Citation Formats

Sahu, Dojalisa, E-mail: dojalisa.sahu@gmail.com, Panda, Nihar Ranjan, E-mail: dojalisa.sahu@gmail.com, Panda, A. K., and Acharya, B. S. Microstructural and optical studies on sonochemically synthesized Cu doped ZnO nanoparticles. United States: N. p., 2014. Web. doi:10.1063/1.4872571.
Sahu, Dojalisa, E-mail: dojalisa.sahu@gmail.com, Panda, Nihar Ranjan, E-mail: dojalisa.sahu@gmail.com, Panda, A. K., & Acharya, B. S. Microstructural and optical studies on sonochemically synthesized Cu doped ZnO nanoparticles. United States. doi:10.1063/1.4872571.
Sahu, Dojalisa, E-mail: dojalisa.sahu@gmail.com, Panda, Nihar Ranjan, E-mail: dojalisa.sahu@gmail.com, Panda, A. K., and Acharya, B. S. Thu . "Microstructural and optical studies on sonochemically synthesized Cu doped ZnO nanoparticles". United States. doi:10.1063/1.4872571.
@article{osti_22269439,
title = {Microstructural and optical studies on sonochemically synthesized Cu doped ZnO nanoparticles},
author = {Sahu, Dojalisa, E-mail: dojalisa.sahu@gmail.com and Panda, Nihar Ranjan, E-mail: dojalisa.sahu@gmail.com and Panda, A. K. and Acharya, B. S.},
abstractNote = {Copper doped ZnO nanoparticles were synthesized by sonochemical method varying the concentration of the impurity. Systematic investigations like X-ray diffraction (XRD) and Transmission electron microscopy (TEM) were carried out to understand the microstructural properties. The average particle sizes and all the crystallographic parameters were calculated from XRD results. This shows the formation of wurtzite phase of ZnO with average size of the particles as 53 nm and an increase of particle size with dopant concentration was also been observed. UV absorption and Fourier transformed infrared spectroscopy (FTIR) spectra revealed the absorption at wavelength < 370 nm with a remarkable red shift of absorption band and a linear decrease of transmittance with increase in doping concentrations respectively.},
doi = {10.1063/1.4872571},
journal = {AIP Conference Proceedings},
number = 1,
volume = 1591,
place = {United States},
year = {Thu Apr 24 00:00:00 EDT 2014},
month = {Thu Apr 24 00:00:00 EDT 2014}
}
  • Highlights: • Cu-doped ZnO nanoparticles obtained by chemical synthesis. • Substitutional or interstitial Cu into ZnO lead specific structural, chemical, and optical changes. • Incorporation efficiency of Cu atoms in ZnO as a function of the Cu concentration in the precursor dissolution. - Abstract: In this work a study of ZnO and Cu-doped ZnO nanoparticles obtained by chemical synthesis in aqueous media was carried out. Structural analysis gave the dominant presence of wurtzite ZnO phase forming a solid solution Zn{sub 1−x}Cu{sub x}O. For high Cu doping CuO phase is also present. For low Cu concentration the lattice shrinks due tomore » Cu atoms substitute Zn atoms. For high Cu concentration the lattice enlarges due to predominance of interstitial Cu. From elemental analysis we determined and analyzed the incorporation efficiency of Cu atoms in Zn{sub 1−x}Cu{sub x}O as a function of the Cu concentration in the precursor dissolution. Combining structural and chemical results we described the Cu/Zn precursor concentrations r{sub w} in which the solid solution of Cu in ZnO is predominant. In the region located at r{sub w} ≈ 0.2–0.3 it is no longer valid. For Cu/Zn precursor concentration r{sub w} > 0.3 interstitial Cu dominates, and some amount of copper oxide appears. As the Cu concentration increases, the effective size of nanoparticles decreases. Photoluminescence (PL) measurements of the Cu-doped ZnO nanoparticles were carried out and analyzed.« less
  • Highlights: • Sonochemical synthesis of iron-doped zinc oxide nanoparticles. • Green synthesis without alkali at room temperature. • Characterization by UV–vis spectroscopy, FESEM, XRD and EDX. • Influence of precursor composition on characteristics. • Composition and characteristics are correlated. - Abstract: Iron-doped zinc oxide nanoparticles have been synthesized sonochemically from aqueous acetyl acetonate precursors of different proportions. Synthesized nanoparticles were characterized with UV–vis spectroscopy, X-ray diffraction and microscopy. Influences of precursor mixture on the characteristics have been examined and modeled. Linear correlations have been proposed between dopant dosing, extent of doping and band gap energy. Experimental data corroborated with themore » proposed models.« less
  • Pure and Co-doped zinc oxide nanomaterials were prepared by a simple low temperature synthesis and were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), high resolution-transmission electron microscopy (HR-TEM), diffused reflectance spectroscopy (DRS) and electron paramagnetic resonance (EPR) techniques. The results showed the formation of nanobushes that consists of several nanowires for pure ZnO and the nanorods formed by self-aggregation for Co-doped ZnO. The presence of Co{sup 2+} ions replacing some of the Zn{sup 2+} in the ZnO lattice was confirmed by EPR and DRS studies. The mechanism for the formation of self-aggregated and self-aligned ZnO rods after themore » incorporation of cobalt in the lattice by the building block units is discussed in this study. Morphological studies were carried out using SEM and HR-TEM, which supports the validity of the proposed mechanism for the formation of ZnO nanobushes and Co-doped ZnO nanorods. The synthesized nanomaterials were found to have good optoelectronic properties.« less
  • The sonochemical method was developed to synthesize uniform SAPO-34 (silicoaluminophosphate molecular sieve) nanoparticles with high crystallinity using TEAOH as a structure-directing agent (SDA). The physicochemical characteristics of SAPO-34 products, i.e. crystallinity, particle size and shape can be controlled by varying the ultrasonic-related variable such as ultrasound power intensity, ultrasonic irradiation time, sonication temperature and geometrical characteristics of the ultrasonic device (e.g., sonotrode size). The products were characterized by XRD, SEM, TEM and BET. It is found that each of the parameters can play a significant role in acoustic cavitation, number of nuclei and the crystal growth. The experimental data establishmore » that the crystallinity is related to ultrasonic intensity and diameter of the sonotrode, as well as sonication temperature. By increasing the ultrasonic power, duration and the sonication temperature, the mean sizes of particles decrease and the morphology of the products efficiently alters from spherical aggregates of cube type SAPO-34 particles to uniform spherical nanoparticles. - Graphical abstract: Increasing US power by increasing either US power intensity or the sonotrode diameter leads to smaller particle size and the morphology changes from spherical aggregates of cubic particles to uniform nanospheres. Highlights: • Effects of ultrasonic parameters on sonochemical synthesis of SAPO-34 nanoparticles. • The higher crystallinity by increasing ultrasonic power, duration and sonication temperature. • The morphology changes from spherical aggregates of cubic particles to uniform nanospheres. • Decreasing the particle size by increasing ultrasonic power, duration and sonication temperature.« less
  • This paper outlines the synthesis and characterization of Ni-Fe co-doped ZnO nanoparticles by facile solution combustion method. The structural characterization by XRD confirmed the phase purity of the samples. Surface morphology studied by scanning electron microscope revealed cubic type shape of grains. EDS analysis conformed the elemental composition. Higher value of DC electrical conductivity and less band gap for co-doped ZnO from UV-Vis studies confirmed the change in defect chemistry of ZnO Matrix.