Title: Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er)

Abstract

Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze (TTB) structure are synthesized using a conventional glass crystallization technique in 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} (mol%) (RE=Sm, Eu, Gd, Dy, and Er) glasses. One sharp crystallization peak is observed at {approx}670 Degree-Sign C in both powdered and bulk glasses, and the formation of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with unit cell parameters of a{approx}1.24 nm and c{approx}0.39 nm was confirmed. It is found from high resolution transmission electron microscope observations that the morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Their average particle size is in the range of 15-60 nm and decreases with decreasing ionic radius of RE{sup 3+} being present in the precursor glasses. The optical transparent crystallized glass (bulk) shows the total photoluminescence (PL) quantum yield of 53% in the visible region of Eu{sup 3+} ions, suggesting a high potential of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals as PL materials. - Graphical abstract: This figure shows a TEM photograph for the heat-treated (667 Degree-Sign C, 3 h) sample of 2.3Dy{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3}. An ellipsoidal-shaped Ba{sub 1-x}Dy{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystal with diameters of 17 and 28more » nm is observed. The ellipsoidal morphology is a common feature in Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals synthesized by the crystallization of 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} glasses. Highlights: Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze structure are synthesized. Black-Right-Pointing-Pointer A glass crystallization technique was applied. Black-Right-Pointing-Pointer The morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Black-Right-Pointing-Pointer The average particle size with 15-60 nm decreases with decreasing ionic radius of RE{sup 3+}. Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals have a high potential as photoluminescence materials.« less

Authors:
; ; ;  [1]
  1. Department of Materials Science and Technology, Nagaoka University of Technology, 1603-1 Kamitomioka-cho, Nagaoka 940-2188 (Japan)
Publication Date:
OSTI Identifier:
22149959
Resource Type:
Journal Article
Journal Name:
Journal of Solid State Chemistry
Additional Journal Information:
Journal Volume: 196; Other Information: Copyright (c) 2012 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); Journal ID: ISSN 0022-4596
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE; 77 NANOSCIENCE AND NANOTECHNOLOGY; 37 INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; BARIUM OXIDES; BORON OXIDES; CRYSTALLIZATION; EUROPIUM IONS; GLASS; MORPHOLOGY; NANOSTRUCTURES; NIOBATES; NIOBIUM OXIDES; PARTICLE SIZE; PHOTOLUMINESCENCE; TRANSMISSION ELECTRON MICROSCOPY; TUNGSTEN BRONZE

Citation Formats

Ida, H., Shinozaki, K., Honma, T., Oh-ishi, K., and Komatsu, T., E-mail: komatsu@mst.nagaokaut.ac.jp. Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er). United States: N. p., 2012. Web. doi:10.1016/J.JSSC.2012.07.006.
Ida, H., Shinozaki, K., Honma, T., Oh-ishi, K., & Komatsu, T., E-mail: komatsu@mst.nagaokaut.ac.jp. Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er). United States. doi:10.1016/J.JSSC.2012.07.006.
Ida, H., Shinozaki, K., Honma, T., Oh-ishi, K., and Komatsu, T., E-mail: komatsu@mst.nagaokaut.ac.jp. Sat . "Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er)". United States. doi:10.1016/J.JSSC.2012.07.006.
@article{osti_22149959,
title = {Synthesis and morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with tungsten bronze structure in RE{sub 2}O{sub 3}-BaO-Nb{sub 2}O{sub 5}-B{sub 2}O{sub 3} glasses (RE: Sm, Eu, Gd, Dy, Er)},
author = {Ida, H. and Shinozaki, K. and Honma, T. and Oh-ishi, K. and Komatsu, T., E-mail: komatsu@mst.nagaokaut.ac.jp},
abstractNote = {Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze (TTB) structure are synthesized using a conventional glass crystallization technique in 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} (mol%) (RE=Sm, Eu, Gd, Dy, and Er) glasses. One sharp crystallization peak is observed at {approx}670 Degree-Sign C in both powdered and bulk glasses, and the formation of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with unit cell parameters of a{approx}1.24 nm and c{approx}0.39 nm was confirmed. It is found from high resolution transmission electron microscope observations that the morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Their average particle size is in the range of 15-60 nm and decreases with decreasing ionic radius of RE{sup 3+} being present in the precursor glasses. The optical transparent crystallized glass (bulk) shows the total photoluminescence (PL) quantum yield of 53% in the visible region of Eu{sup 3+} ions, suggesting a high potential of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals as PL materials. - Graphical abstract: This figure shows a TEM photograph for the heat-treated (667 Degree-Sign C, 3 h) sample of 2.3Dy{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3}. An ellipsoidal-shaped Ba{sub 1-x}Dy{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystal with diameters of 17 and 28 nm is observed. The ellipsoidal morphology is a common feature in Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals synthesized by the crystallization of 2.3RE{sub 2}O{sub 3}-27.4BaO-34.3Nb{sub 2}O{sub 5}-36B{sub 2}O{sub 3} glasses. Highlights: Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals with a tetragonal tungsten bronze structure are synthesized. Black-Right-Pointing-Pointer A glass crystallization technique was applied. Black-Right-Pointing-Pointer The morphology of Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals is ellipsoidal. Black-Right-Pointing-Pointer The average particle size with 15-60 nm decreases with decreasing ionic radius of RE{sup 3+}. Black-Right-Pointing-Pointer Ba{sub 1-x}RE{sub 2x/3}Nb{sub 2}O{sub 6} nanocrystals have a high potential as photoluminescence materials.},
doi = {10.1016/J.JSSC.2012.07.006},
journal = {Journal of Solid State Chemistry},
issn = {0022-4596},
number = ,
volume = 196,
place = {United States},
year = {2012},
month = {12}
}