Electrochromism in sputtered WO{sub 3} thin films
- Pilkington Technology Centre, Ormskirk (United Kingdom)
There are large variations in the properties of WO{sub 3} sputtered under different conditions and two samples sputtered from an oxide target and reactively sputtered from a metal target were compared in detail. The thin film sputtered from an oxide target was found to color and bleach rapidly in 1 M LiClO{sub 4} in propylene carbonate, while the thin film reactively sputtered from a metal target could be colored deeply, but bleached only slowly. By calculating the rate of change of optical density during cyclic voltammetry, it was possible to directly compare the coloration response with the current/voltage behavior of the electrodes. In both cases at least two lithium insertion reactions appear to occur. The distinction between the two reactions was especially clear in the sample sputtered from a metal target, in which an insertion of high electrochromic efficiency occurred up to Li{sub 0.2}WO{sub 3} and then an insertion of considerably lower electrochromic efficiency up to Li{sub 0.5}WO{sub 3}. Although a small amount of coloration and bleaching continued to occur after switching the reactively sputtered sample to open circuit during the coloration and bleaching cycles; transmission change was largely halted by disconnecting the external current supply. The slow end to the bleach of the reactively sputtered sample corresponded to a reaction of high electrochromic efficiency.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 220883
- Journal Information:
- Journal of the Electrochemical Society, Vol. 143, Issue 3; Other Information: PBD: Mar 1996
- Country of Publication:
- United States
- Language:
- English
Similar Records
Electrochromic properties of sputtered amorphous films in the systems WO/sub 3/-Nb/sub 2/O/sub 5/ and Li/sub 2/O-WO/sub 3/-Nb/sub 2/O/sub 5/
Effects of surface porosity on tungsten trioxide (WO{sub 3}) films' electrochromic performance