3D characterization of intermetallics in a high pressure die cast Mg alloy using focused ion beam tomography
- ARC Centre of Excellence for Design in Light Metals, Materials Engineering, University of Queensland, Brisbane, QLD 4072 (Australia)
- Electron Microscope Unit, UNSW Analytical Centre, University of New South Wales, Sydney, NSW 2052 (Australia)
The degree of spatial interconnection of the Mg{sub 17}Al{sub 12} ({beta}-phase) intermetallic in a Mg-9Al-1Zn alloy was assessed through serial sectioning at the centre and near a corner in a casting cross-section. The three dimensional reconstructions showed that the intermetallics were profusely interconnected forming a scaffold-like network over the entire cross-section, but especially near the casting surface. The scale and degree of the interconnection appeared determined by the local concentration of large dendritic grains injected from the shot sleeve. The volume fractions of intermetallics obtained through the 3D reconstruction indicated a higher content of {beta}-phase at the corner regions in comparison with the core. The volume fractions obtained by FIB were consistent with theoretical and experimental values obtained using other techniques.
- OSTI ID:
- 22066228
- Journal Information:
- Materials Characterization, Vol. 61, Issue 11; Other Information: Copyright (c) 2010 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved.; Country of input: International Atomic Energy Agency (IAEA); ISSN 1044-5803
- Country of Publication:
- United States
- Language:
- English
Similar Records
Enhancements in Magnesium Die Casting Impact Properties
The Effects of Grain Refinement and Rare Earth Intermetallics on Mechanical Properties of As-Cast and Wrought Magnesium Alloys