Characteristics of Hf-silicate thin films synthesized by plasma enhanced atomic layer deposition
- Department of Chemical and Biomolecular Engineering, University of California, Los Angeles, California 90095 (United States)
Hafnium silicate films were grown by alternating the deposition cycles of hafnium oxide and silicon oxide using a plasma enhanced atomic layer deposition process. The as-deposited and 900 deg. C annealed hafnium silicate films were determined to be amorphous using grazing incidence x-ray diffraction. This suggested that the formation of hafnium silicate suppressed the crystallization of HfO{sub 2} at high temperatures. The dielectric constants increased from {approx}5 to {approx}17 as the hafnium content increased from 9 to 17 at. % in the hafnium silicate films. The leakage currents through the Hf-rich Hf-silicate films were two to three orders of magnitude lower than that of SiO{sub 2} with the same equivalent oxide thickness in the range of 1.6-2.3 nm. The estimated band gap of Hf-silicate films from the O 1s plasma loss spectra increased with the increasing Si content due to the higher band gap of SiO{sub 2} than that of HfO{sub 2}.
- OSTI ID:
- 21192420
- Journal Information:
- Journal of Vacuum Science and Technology. A, International Journal Devoted to Vacuum, Surfaces, and Films, Vol. 26, Issue 5; Other Information: DOI: 10.1116/1.2966430; (c) 2008 American Vacuum Society; Country of input: International Atomic Energy Agency (IAEA); ISSN 1553-1813
- Country of Publication:
- United States
- Language:
- English
Similar Records
X-ray Photoemission and X-ray Absorption Studies of Hf-silicate Dielectric Layers
Characteristics of HfO{sub 2} thin films grown by plasma atomic layer deposition