Single crystal X-ray diffraction studies on [(CH{sub 3}){sub n}NH{sub 4-n}]{sub 3}[Sb{sub 2}Cl{sub 9}] (n=2, 3) chloroantimonates(III) in their low-temperature ferroelectric phases-structures and phase transitions
- Crystallography Laboratory, Department of Geosciences, Virginia Tech, Blacksburg, VA 24061 (United States)
The structures of two ferroic chloroantimonates(III): [(CH{sub 3}){sub 2}NH{sub 2}]{sub 3}[Sb{sub 2}Cl{sub 9}] (DMACA) and [(CH{sub 3}){sub 3}NH]{sub 3}[Sb{sub 2}Cl{sub 9}] (TMACA) were determined in their low-temperature phases. The structure of DMACA was investigated at 100 and 15K, and TMACA at 15K. The structures consist of two-dimensional inorganic layers and organic cations bound together by the N(C)-H...Cl hydrogen bonds. All of the organic cations in both compounds at all studied temperatures are ordered. There is no indication of the structural phase transition in the structure of DMACA below 242K. The geometry and distortions of the [SbCl{sub 6}]{sup 3-} octahedra in both compounds is discussed. The monoclinic Pc space group was found for both compounds: DMACA a=9.3590(5), b=9.0097(4), c=14.1308(7)A, {beta}=95.229(4){sup o}, R{sub 1}=0.0240, wR{sub 2}=0.0491 and a=9.3132(4), b=9.0008(3), c=14.1088(5)A, {beta}=95.010(3){sup o}, R{sub 1}=0.0230, wR{sub 2}=0.0482 at 100 and 15K, respectively; TMACA a=9.8652(5), b=9.1129(4), c=15.0964(7)A, {beta}=89.988(4){sup o}, R{sub 1}=0.0239, wR{sub 2}=0.0611 at 15K.
- OSTI ID:
- 20729022
- Journal Information:
- Journal of Solid State Chemistry, Vol. 178, Issue 7; Other Information: DOI: 10.1016/j.jssc.2005.04.020; PII: S0022-4596(05)00175-1; Copyright (c) 2005 Elsevier Science B.V., Amsterdam, The Netherlands, All rights reserved; Country of input: International Atomic Energy Agency (IAEA); ISSN 0022-4596
- Country of Publication:
- United States
- Language:
- English
Similar Records
Low-temperature single crystal X-ray diffraction and high-pressure Raman studies on [(CH{sub 3}){sub 2}NH{sub 2}]{sub 2}[SbCl{sub 5}]
[H{sub 3}N(CH{sub 2}){sub 4}NH{sub 3}]{sub 2}[Al{sub 4}(C{sub 2}O{sub 4})(H{sub 2}PO{sub 4}){sub 2}(PO{sub 4}){sub 4}].4[H{sub 2}O]: A new layered aluminum phosphate-oxalate