Competition between tensile and compressive stress mechanisms during Volmer-Weber growth of aluminum nitride films
- Brown University, Division of Engineering, Providence, Rhode Island 02912 (United States)
Stress evolution during molecular-beam epitaxy of AIN films was monitored with in situ curvature measurements. Changes in the growth rate produced large stress variations, with more tensile stress observed at higher growth rates. For example, at a growth temperature of 750 deg. C the instantaneous steady-state stress in films with similar grain sizes varied from -0.15 GPa at a growth rate of 90 nm/h, to approximately 1.0 GPa at a growth rate of 300 nm/h. To explain these results, we develop a kinetic model of stress evolution that describes both tensile and compressive mechanisms. The tensile component is based on a mechanism which is proposed here as an inherent feature of grain-boundary formation. The compressive component is based on our recent model of atom insertion, driven by the excess chemical potential of surface adatoms that is created by the growth flux. The combined model predicts that the stress is largely governed by the competition between tensile and compressive mechanisms, which can be conveniently described with a single parameter, {alpha}. The limiting values {alpha}{yields}0 and {alpha}{yields}+{infinity} correspond to previous models of compressive and tensile stresses, respectively.
- OSTI ID:
- 20714057
- Journal Information:
- Journal of Applied Physics, Vol. 98, Issue 4; Other Information: DOI: 10.1063/1.1994944; (c) 2005 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
The dynamic competition between stress generation and relaxation mechanisms during coalescence of Volmer--Weber thin films
Interdependence between stress, preferred orientation, and surface morphology of nanocrystalline TiN thin films deposited by dual ion beam sputtering