Heteroepitaxial growth of In-face InN on GaN (0001) by plasma-assisted molecular-beam epitaxy
- Microelectronics Research Group, Physics Department, University of Crete, P.O. Box 2208, 71003 Heraklion-Crete (Greece) and Foundation for Research and Technology-Hellas (FORTH), Institute of Electronic Structure and Laser (IESL), P.O. Box 1527, 71110 Heraklion-Crete (Greece)
The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less than 350 deg. C and of the Stranski-Krastanov for substrate temperatures between 350 and 520 deg. C. The number of monolayers of initial two-dimensional growth, in the case of Stranski-Krastanov mode, varies monotonically with substrate temperature, from 2 ML at 400 deg. C to about 12 ML at 500 deg. C. The evolution and coalescence of nucleated islands were also investigated as a function of substrate temperature. It was found that at higher temperature their coalescence is inhibited leading to porous-columnar InN thin films, which exhibit growth rates higher than the nominal value. Therefore, in order to achieve continuous InN layers on GaN (0001) a two-step growth approach is introduced. In that approach, InN is nucleated at low temperatures on GaN and the growth continues until full coalescence of the nucleated islands. Subsequently, this nucleation layer is overgrown at higher substrate temperature in order to achieve high-quality continuous films. The InN films grown by the two-step method were investigated by x-ray diffraction, Hall-effect measurements, and transmission electron microscopy. It was found that the lattice mismatch between InN and GaN is almost completely accommodated by the development of a misfit dislocation network at the interface. Optimum group-III to active nitrogen flux ratios and substrate temperature conditions were identified for the two-step growth process. Films, grown under those conditions, exhibited full width at half maximum of x-ray rocking curves at (0004) and (1015) diffractions equal to 360 and 435 arc sec, respectively. Room-temperature Hall mobility was found to depend sensitively on the group-III to active nitrogen flux ratio during growth of the main step and to be independent of the structural properties of the films. Mobilities up to 860 cm{sup 2}/V s at carrier concentration of 1.6x10{sup 19} cm{sup -3} were measured.
- OSTI ID:
- 20711715
- Journal Information:
- Journal of Applied Physics, Vol. 97, Issue 11; Other Information: DOI: 10.1063/1.1923166; (c) 2005 American Institute of Physics; Country of input: International Atomic Energy Agency (IAEA); ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth mechanism and microstructure of low defect density InN (0001) In-face thin films on Si (111) substrates
In situ revelation of a zinc-blende InN wetting layer during Stranski-Krastanov growth on GaN(0001) by molecular-beam epitaxy
Related Subjects
ATOMIC FORCE MICROSCOPY
CARRIER DENSITY
COALESCENCE
CRYSTAL GROWTH
DECOMPOSITION
DESORPTION
DISLOCATIONS
ELECTRON DIFFRACTION
GALLIUM NITRIDES
HALL EFFECT
INDIUM
INDIUM NITRIDES
MOLECULAR BEAM EPITAXY
NUCLEATION
POROUS MATERIALS
TEMPERATURE RANGE 0273-0400 K
TEMPERATURE RANGE 0400-1000 K
THIN FILMS
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION