Surface structure and electrochemical characteristics of Ti-V-Cr bcc-type solid solution alloys sintered with Ni
Ti-V-Cr bcc-type solid solution alloys can absorb a large amount of hydrogen and be applied to active materials of the negative electrode in Ni-MH batteries. However, because of the insolubility of Ni into these alloys, the electrochemical characteristics like discharge capacity and cycle life were poor. In order to increase the discharge capacity of hydrogen absorbing alloy electrodes, Ti-V-Cr bcc-type alloy powders were sintered with Ni in order to form Ni contained surface layer on the alloy surface. As sintering temperature rose up, the surface composition changed from TiNi to Ti{sub 2}Ni. TiNi surface layer showed better electrochemical characteristics. For the Ni adding method, Ni electroless plating was preferred because of good adhesion. As a result of optimized conditions, a discharge capacity of 570 mAh/g and an improvement of cycle life were achieved.
- Research Organization:
- Matsushita Electric Industrial Co., Ltd., Osaka (JP)
- OSTI ID:
- 20086881
- Resource Relation:
- Conference: 1999 Materials Research Society Spring Meeting, San Francisco, CA (US), 04/05/1999--04/08/1999; Other Information: PBD: 2000; Related Information: In: New materials for batteries and fuel cells. Materials Research Society symposium proceedings, Volume 575, by Doughty, D.H.; Nazar, L.F.; Arakawa, Masayasu; Brack, H.P.; Naoi, Katsuhiko [eds.], 454 pages.
- Country of Publication:
- United States
- Language:
- English
Similar Records
The role of Li{sub 2}MO{sub 2} structures (m = metal) in the electrochemistry of (chi)LiMn{sub 0.5}Ni{sub 0.5}O{sub 2} {center_dot} (1 - chi)Li(sub 2}TiO{sub 3} electrodes for lithium-ion batteries.
Activation characteristics of multiphase Zr-based hydrogen storage alloys for Ni/MH rechargeable batteries