Title: Grain size and temperature dependence of superplastic deformation in an Al-Mg alloy under isostructural condition

Journal Article · · Acta Materialia

The mechanical behavior of a superplastic Al-4.7% Mg-0.8% Mn-0.4% Cu alloy has been characterized by a new type of step train-rate test which preserves the initial microstructure of the alloy (i.e. an isostructural test). Four different grain sizes of the alloy (8--30 {micro}m), prepared by variations in thermomechanical processing practice, were examined. A sigmoidal relationship between log {sigma} and log {dot {var_epsilon}} is observed for each isostructural condition. The value of maximum m (=dlog {sigma}/dlog {dot {var_epsilon}}) increased with increasing temperature and with decreasing grain size. The isostructural log {sigma} vs log {dot {var_epsilon}} data are evaluated using the grain mantle based quantitative model proposed by Ghosh. In the dislocation creep region ({dot {var_epsilon}} > 10{sup {minus}1}/s), the stress exponent is 4.55 and activation energy is close to that for lattice self-diffusion, but the grain size exponent is non-zero ({approximately}0.37). In the grain mantle deformation region ({dot {var_epsilon}} <10{sup {minus}3}/s), the value of the stress exponent based on effective stress ({sigma} - {sigma}{sub 0} is threshold stress) is {approximately} 1.7, and the grain size exponent is 2.3; but interestingly activation energy is the same as that for dislocation creep. Grain mantle creep is now also believed to be controlled by dislocation glide and climb processes, but its rate is enhanced many times due to a high concentration of vacancies near grain boundaries. {sigma}{sub 0}computed based on the model shows that it increases with increasing grain size and with decreasing temperature.

Research Organization:
Univ. of Michigan, Ann Arbor, MI (US)
Sponsoring Organization:
USDOE; US Department of the Air Force
DOE Contract Number:
FG02-96ER45608
OSTI ID:
20020576
Journal Information:
Acta Materialia, Vol. 48, Issue 6; Other Information: PBD: 3 Apr 2000; ISSN 1359-6454
Country of Publication:
United States
Language:
English

Similar Records

Superplastic deformation behavior of 8090 aluminum-lithium alloy
Journal Article · Wed Mar 15 00:00:00 EST 1995 · Scripta Metallurgica et Materialia · OSTI ID:20020576

Superplastic deformation of Zr{sub 65}Al{sub 10}Ni{sub 10}Cu{sub 15} metallic glass
Journal Article · Fri Aug 15 00:00:00 EDT 1997 · Scripta Materialia · OSTI ID:20020576

Creep study of mechanisms involved in low-temperature superplasticity of UFG Ti-6Al-4V processed by SPD
Journal Article · Wed Jun 15 00:00:00 EDT 2016 · Materials Characterization · OSTI ID:20020576