Investigating the degradation mechanism of the solid oxide fuel cell nickel-yttria stabilized zirconia anode under siloxane contamination
Journal Article
·
· Journal of Power Sources
Not provided.
- Research Organization:
- Arizona State Univ., Tempe, AZ (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- EE0007721
- OSTI ID:
- 1848561
- Journal Information:
- Journal of Power Sources, Vol. 480, Issue C; ISSN 0378-7753
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
Similar Records
Investigating the degradation mechanism of the solid oxide fuel cell nickel-yttria stabilized zirconia anode under siloxane contamination
Failure analysis of solid oxide fuel cells nickel-yttria stabilized zirconia anode under siloxane contamination
Degradation Comparison of Cyclic and Linear Siloxane Contamination on Solid Oxide Fuel Cells Ni-YSZ Anode
Journal Article
·
Tue Nov 03 00:00:00 EST 2020
· Journal of Power Sources
·
OSTI ID:1848561
Failure analysis of solid oxide fuel cells nickel-yttria stabilized zirconia anode under siloxane contamination
Journal Article
·
Sat Oct 01 00:00:00 EDT 2022
· Electrochimica Acta
·
OSTI ID:1848561
Degradation Comparison of Cyclic and Linear Siloxane Contamination on Solid Oxide Fuel Cells Ni-YSZ Anode
Journal Article
·
Fri Oct 22 00:00:00 EDT 2021
· Frontiers in Energy Research
·
OSTI ID:1848561