Colossal Grains for a New Structural Paradigm in Thin-Film Photovoltaics
II-VI based thin-film photovoltaics (PV) have experienced substantial commercial success on a foundation of fast large-scale deposition and processing. This type of processing, regardless of material type, nearly always results in small grain (nm to several um diameters) polycrystalline material that, if not for effective grain boundary (GB) and defect passivation, would severely limit PV performance. In the case of CdTe based PV technology, the nearly ubiquitous CdCl2 treatment is used, in part, to passivate the polycrystalline p-type absorber even though Cl is known to (and used to) compensate p-type II-VI materials. Given that VOC is still the most limited performance metric and it can only be improved through higher p-type absorber concentrations, CdCl2 treatments may be holding the technology back. In this talk, we will discuss results related to a process by which small grain CdSeTe material is rapidly transformed into very large grain material (100-1000um diameters, Fig. 1a). This explosive recrystallization, which we have termed colossal grain growth (CGG), occurs by a Cl free process with thin films (<10um) deposited using the same fast deposition techniques the industry has relied on for more than a decade. Our modeling suggests that GB recombination becomes significantly less important at these grain sizes and thus may eliminate the need for a CdCl2 treatment. This result is complimented by previous results of epitaxial growth at high rates on single crystal seed layers. Thin CdSeTe CGG seed layers can be used for rapid epitaxy of CdTe to complete a standard device stack (Fig.1b). This is an optimistic view and the current limitations and challenges related to this process and these materials will also be discussed, including alloy and substrate roughness sensitivity, intragrain material quality, and complex defect chemistry. These challenges are not insignificant but overcoming them may enable a new structural paradigm for thin-film PV.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE), Renewable Power Office. Solar Energy Technologies Office
- DOE Contract Number:
- AC36-08GO28308
- OSTI ID:
- 1823440
- Report Number(s):
- NREL/PR-5K00-80918; MainId:78696; UUID:2012922c-703a-4ef2-bd74-d53f6a9057a3; MainAdminID:61841
- Resource Relation:
- Conference: Presented at the 22nd American Conference on Crystal Growth and Epitaxy, 2-4 August 2021
- Country of Publication:
- United States
- Language:
- English
Similar Records
Luminescence methodology to determine grain-boundary, grain-interior, and surface recombination in thin-film solar cells
STEM characterization of solar cells