Journal Article · · Progress in Nuclear Energy
 [1];  [1];  [1];  [1];  [1]
  1. BATTELLE (PACIFIC NW LAB)
+ Show Author Affiliations

This work investigates the effects of casting parameter changes on as-cast uranium-10 wt% molybdenum alloys on a 1-2kg scale. A commercial tilt-pour vacuum induction melting system was utilized to study the effects of casting atmosphere, total heating time, hold time at maximum temperature, mold temperature, and crucible type on the as-cast microstructure of U-10Mo. Ten thin plates (5.08 mm thick) and four thick plates (25.4 mm and 63.5 mm thick) were cast and analyzed for carbon, oxygen, hydrogen, and nitrogen impurities. Additionally, molybdenum content and primary dendrite length (PDL) of the microstructure was quantified. A statistical evaluation was performed to identify key carbon and oxygen relationships with operating parameters, impurities, and primary dendrite length. Additional factors investigated include: crucible material, time at maximum temperature, total heating time, and pour temperature. Zirconia crucibles reduced carbon content on average by 35%. Additionally, there was a significant statistical association between carbon and oxygen content, between oxygen content and maximum temperature hold time, between mold temperature and PDL, and between PDL, maximum temperature hold time and mold temperature.

Research Organization:
Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
Sponsoring Organization:
USDOE
DOE Contract Number:
AC05-76RL01830
OSTI ID:
1820958
Report Number(s):
PNNL-SA-155216
Journal Information:
Progress in Nuclear Energy, Vol. 140
Country of Publication:
United States
Language:
English

References (13)

Constitution of low carbon U-C alloys September 1960
A US perspective on fast reactor fuel fabrication technology and experience part I: metal fuels and assembly design June 2009
Microstructural characteristics of DU–xMo alloys with x=7–12wt% June 2009
Metallic fuels for advanced reactors July 2009
Effect of second phase particles and stringers on microstructures after rolling and recrystallization October 2018
Grain control in mechanically alloyed oxide dispersion strengthened MA 957 steel October 1993
Beta-phase retention in uranium alloys February 1990
Short communication on Kinetics of grain growth and particle pinning in U-10 wt.% Mo January 2018
Metallic fast reactor fuels January 1997
Use of Tribocor 532N for a carbon-free induction furnace for vacuum-induction melting and casting of uranium and its alloys November 1987
Thermomechanical process optimization of U-10 wt% Mo – Part 1: high-temperature compressive properties and microstructure October 2015
An analysis of strengthening mechanisms in a mechanically alloyed, oxide dispersion strengthened iron aluminide intermetallic June 2002
Phase transformation of metastable cubic γ-phase in U–Mo alloys September 2010

Similar Records

Related Subjects