Boundary in {gamma}{double_prime} precipitates in Inconel 718 nickel-base superalloy
Journal Article
·
· Acta Metallurgica et Materialia
- Tsinghua Univ., Beijing (China). Dept. of Materials Science and Engineering
- Chugoku National Industrial Research Inst., Kure, Hiroshima (Japan)
The coalesced {gamma}{double_prime} precipitate in the aged nickel-base superalloy has been investigated using a high resolution electron microscopy. The encounter of {gamma}{double_prime} precipitates during aging formed the coalesced precipitate that consists of several domains which keep the original orientation before encountering. The thickness of boundary in the coalesced {gamma}{double_prime} precipitate was in the range of zero to a few atom layers.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 178007
- Journal Information:
- Acta Metallurgica et Materialia, Vol. 43, Issue 12; Other Information: PBD: Dec 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Coarsening behavior of {gamma}{double_prime} precipitates in modified Inconel 718 superalloy
Relationship between the lattice constant of {Upsilon} phase and the content of {delta} phase, {gamma}{double_prime} and {gamma}{prime} phases in Inconel 718
Grain boundary {gamma}{double_prime} precipitation and niobium segregation in Inconel 718
Journal Article
·
Fri Dec 15 00:00:00 EST 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:178007
Relationship between the lattice constant of {Upsilon} phase and the content of {delta} phase, {gamma}{double_prime} and {gamma}{prime} phases in Inconel 718
Journal Article
·
Tue Jul 01 00:00:00 EDT 1997
· Scripta Materialia
·
OSTI ID:178007
+3 more
Grain boundary {gamma}{double_prime} precipitation and niobium segregation in Inconel 718
Journal Article
·
Sat Apr 01 00:00:00 EST 1995
· Scripta Metallurgica et Materialia
·
OSTI ID:178007