Over 11% Efficient Eco-Friendly Kesterite Solar Cell: Effects of S-Enriched Surface of Cu2ZnSn(S,Se)4 Absorber and Band Gap Controlled (Zn,Sn)O Buffer
For high efficiency kesterite Cu2ZnSn(S,Se)4 (CZTSSe) solar cell, CdS thin film was usually used as a buffer layer. However, due to the toxicity of Cd and pollution problems involved from the solution-based chemical bath deposition, eco-friendly high efficiency CZTSSe solar cell with Cd-free buffer is necessary. As an Cd-free buffer layer, we investigated (Zn,Sn)O (ZTO) film deposited by sputtering method. In order to achieve high power conversion efficiency, we controlled energy band gaps of CZTSSe absorber as well as ZTO buffer, which was required to optimize conduction band offset (CBO) between the absorber and the buffer and to increase open circuit voltage (Voc) and fill factor (FF). The CBO was optimized by controlling the band gap of ZTO. By varying the Sn/(Zn + Sn) ratio and its deposition temperature, band gap of ZTO was successfully adjusted. Experimental and computational calculation results showed that solar cell performance was strongly affected by the CBO between absorber and buffer. Besides CBO matching, larger band gap of ZTO improved short circuit current density (Jsc) with enhanced external quantum efficiency value in blue photon spectrum range. As an additional way to improve power conversion efficiency of solar cell, band graded CZTSSe absorber was developed by using spray-based two-step process. The sprayed CZTSSe film was engineered to have S-enriched surface, which makes surface band gap widened and surface passivated, and resultantly increases Voc, Jsc and fill factor (FF). By controlling band gaps of both CZTSSe absorber and ZTO buffer, we obtained 11.22% environment-friendly CZTSSe solar cell without MgF2 anti-reflection coating.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- DE-AC36-08GO28308
- OSTI ID:
- 1665829
- Report Number(s):
- NREL/JA-5900-77813; MainId:30728; UUID:27690dba-0c64-4d5f-9d02-d9c1ac2c5e7c; MainAdminID:17430
- Journal Information:
- Nano Energy, Vol. 78
- Country of Publication:
- United States
- Language:
- English
Similar Records
Band alignments of different buffer layers (CdS, Zn(O,S), and In{sub 2}S{sub 3}) on Cu{sub 2}ZnSnS{sub 4}
CdS and Cd-Free Buffer Layers on Solution Phase Grown Cu2ZnSn(SxSe1- x)4 :Band Alignments and Electronic Structure Determined with Femtosecond Ultraviolet Photoemission Spectroscopy