Title: Initial Stages of Na2SO4-Induced Degradation of β-Ni–36Al at 700 °C: I-Intrinsic Behavior

Abstract

Not provided.

Authors:
ORCiD logo; ; ;
Publication Date:
Research Org.:
Univ. of Pittsburgh, PA (United States)
Sponsoring Org.:
USDOE Office of Fossil Energy (FE)
OSTI Identifier:
1537774
DOE Contract Number:  
FE0007271
Resource Type:
Journal Article
Journal Name:
Oxidation of Metals
Additional Journal Information:
Journal Volume: 88; Journal Issue: 5-6; Journal ID: ISSN 0030-770X
Publisher:
Springer
Country of Publication:
United States
Language:
English
Subject:
Metallurgy & Metallurgical Engineering

Citation Formats

Zahiri Azar, Maryam, Gheno, Thomas, Gleeson, Brian, and Heuer, Arthur H. Initial Stages of Na2SO4-Induced Degradation of β-Ni–36Al at 700 °C: I-Intrinsic Behavior. United States: N. p., 2017. Web. doi:10.1007/s11085-017-9760-2.
Zahiri Azar, Maryam, Gheno, Thomas, Gleeson, Brian, & Heuer, Arthur H. Initial Stages of Na2SO4-Induced Degradation of β-Ni–36Al at 700 °C: I-Intrinsic Behavior. United States. doi:10.1007/s11085-017-9760-2.
Zahiri Azar, Maryam, Gheno, Thomas, Gleeson, Brian, and Heuer, Arthur H. Fri . "Initial Stages of Na2SO4-Induced Degradation of β-Ni–36Al at 700 °C: I-Intrinsic Behavior". United States. doi:10.1007/s11085-017-9760-2.
@article{osti_1537774,
title = {Initial Stages of Na2SO4-Induced Degradation of β-Ni–36Al at 700 °C: I-Intrinsic Behavior},
author = {Zahiri Azar, Maryam and Gheno, Thomas and Gleeson, Brian and Heuer, Arthur H.},
abstractNote = {Not provided.},
doi = {10.1007/s11085-017-9760-2},
journal = {Oxidation of Metals},
issn = {0030-770X},
number = 5-6,
volume = 88,
place = {United States},
year = {2017},
month = {3}
}

Works referenced in this record:

Second Generation gas Turbine
journal, August 1969


Formation and Reactivity Thermodynamics of Sodium Sulfate With Gas Turbine Alloys
journal, May 1968


Reviewing sulfidation corrosion—Yesterday and today
journal, November 1996


Mechanism of Na[sub 2]SO[sub 4] Induced Corrosion at 600°–900°C
journal, January 1980

  • Luthra, K. L.
  • Journal of The Electrochemical Society, Vol. 127, Issue 10
  • DOI: 10.1149/1.2129375

Thermodynamics of Molten Sulfate Mixtures
journal, January 1982

  • Misra, A. K.
  • Journal of The Electrochemical Society, Vol. 129, Issue 8
  • DOI: 10.1149/1.2124305

A TEM study of sulfur distribution in oxidized Ni40Al and its effect on oxide growth and adherence
journal, April 2007

  • Molins, Régine; Rouzou, Isabelle; Hou, Peggy
  • Materials Science and Engineering: A, Vol. 454-455
  • DOI: 10.1016/j.msea.2006.11.015

Surface science approach of corrosion phenomena
journal, January 1998


Non-protective alumina growth in sulfur-doped NiAl(Zr)
journal, January 2000


Accelerated oxidation, internal oxidation, intergranular oxidation, and pesting of intermetallic compounds
journal, August 1995

  • Grabke, H. J.; Meier, G. H.
  • Oxidation of Metals, Vol. 44, Issue 1-2
  • DOI: 10.1007/BF01046726

Oxide scale adhesion and impurity segregation at the scale/metal interface
journal, December 1992

  • Hou, Peggy Y.; Stringer, John
  • Oxidation of Metals, Vol. 38, Issue 5-6
  • DOI: 10.1007/BF00665658

Sulfur segregation during the high-temperature oxidation of chromium
journal, December 1991

  • Fox, P.; Lees, D. G.; Lorimer, G. W.
  • Oxidation of Metals, Vol. 36, Issue 5-6
  • DOI: 10.1007/BF01151594

Interfacial Segregation, Pore Formation, and Scale Adhesion on NiAl Alloys
journal, February 2005


Adherent Al2O3 scales formed on undoped nicrai alloys
journal, January 1987

  • Smialek, James L.
  • Metallurgical Transactions A, Vol. 18, Issue 1
  • DOI: 10.1007/BF02646237

Some comments on the role of yttrium in protective oxide scale adherence
journal, March 1987


A relationship between indigenous impurity elements and protective oxide scale adherence characteristics
journal, June 1986

  • Smeggil, J. G.; Funkenbusch, A. W.; Bornstein, N. S.
  • Metallurgical Transactions A, Vol. 17, Issue 6
  • DOI: 10.1007/BF02661258

Advances in Coating Design for High-Performance Gas Turbines
journal, September 2003


Reaction morphologies developed by nickel aluminides in type II hot corrosion conditions: The effect of chromium
journal, December 2015


Transmission EBSD from 10 nm domains in a scanning electron microscope: TRANSMISSION EBSD IN THE SEM
journal, November 2011


Transmission EBSD - Bridging the Gap between SEM and TEM
journal, August 2013


Na2SO4-induced accelerated oxidation (hot corrosion) of nickel
journal, July 1970

  • Goebel, J. A.; Pettit, F. S.
  • Metallurgical Transactions, Vol. 1, Issue 7
  • DOI: 10.1007/BF02642794

On the Hot Corrosion of Nickel at 700 °C
journal, August 2015


Sulfidation behaviour of nickel aluminides
journal, December 1996

  • Schramm, B.; Auer, W.
  • Materials and Corrosion/Werkstoffe und Korrosion, Vol. 47, Issue 12
  • DOI: 10.1002/maco.19960471204

High temperature internal oxidation behaviour of dilute Ni-Al alloys
journal, May 1983

  • Hindam, H.; Whittle, D. P.
  • Journal of Materials Science, Vol. 18, Issue 5
  • DOI: 10.1007/BF01111959

Carburization of Fe-Cr Alloys During Oxidation in Dry Carbon Dioxide
journal, January 1967

  • Fujii, C. T.; Meussner, R. A.
  • Journal of The Electrochemical Society, Vol. 114, Issue 5
  • DOI: 10.1149/1.2426622

Scale formation mechanisms of martensitic steels in high CO 2 /H 2 O-containing gases simulating oxyfuel environments
journal, March 2009

  • Pirón Abellán, J.; Olszewski, T.; Penkalla, H. J.
  • Materials at High Temperatures, Vol. 26, Issue 1
  • DOI: 10.3184/096034009X438185