In situ Synthesis and Characterization of Uranium Carbide Using High Temperature Neutron Diffraction
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
We investigated the formation of UCx from UO2+x and graphite in situ using neutron diffraction at high temperatures with particular focus on resolving the conflicting reports on the crystal structure of non-quenchable cubic UC2. The agents were UO2 nanopowder, which closely imitates nano grains observed in spent reactor fuels, and graphite powder. In situ neutron diffraction revealed the onset of the UO2 + 2C → UC + CO2 reaction at 1440 °C, with its completion at 1500 °C. Upon further heating, carbon diffuses into the uranium carbide forming C2 groups at the octahedral sites. This resulting high temperature cubic UC2 phase is similar to the NaCl-type structure as proposed by Bowman et al. Here, our novel experimental data provide insights into the mechanism and kinetics of formation of UC as well as characteristics of the high temperature cubic UC2 phase which agree with proposed rotational rehybridization found from simulations by Wen et al.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- 89233218CNA000001; AC52-06NA25396
- OSTI ID:
- 1492651
- Alternate ID(s):
- OSTI ID: 1359399
- Report Number(s):
- LA-UR-15-24565
- Journal Information:
- Journal of Nuclear Materials, Vol. 471; ISSN 0022-3115
- Publisher:
- ElsevierCopyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Similar Records
Advanced Sample Environments for in situ Neutron Diffraction Studies of Nuclear Materials
STUDY ON THE PREPARTION OF URANIUM CARBIDES