3D time-resolved observations of corrosion and corrosion-fatigue crack initiation and growth in peak-aged Al 7075 using synchrotron X-ray tomography
Journal Article
·
· Corrosion Science
Corrosion fatigue crack initiation and growth from corrosion pits in 7075 aluminium alloys was observed in situ using 3D x-ray synchrotron tomography. Peak-aged Al 7075 was corroded by soaking in 3.5 wt.% NaCl solution, then fatigue tested in situ in the solution using synchrotron X-ray tomography to analyse the corrosion fatigue crack initiation and growth from the pits. Hydrogen bubbles were observed within the intergranular corrosion fatigue cracks, indicating chemical changes in the sample during corrosion fatigue. In situ crack growth, the effect of microstructural constituents on dissolution and growth, and multimodal observations of the fracture surface were conducted and are discussed.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- National Science Foundation (NSF); USDOE Office of Science (SC), Basic Energy Sciences (BES); US Department of the Navy, Office of Naval Research (ONR)
- DOE Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1474321
- Journal Information:
- Corrosion Science, Vol. 138, Issue C; ISSN 0010-938X
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
Similar Records
In situ investigation of high humidity stress corrosion cracking of 7075 aluminum alloy by three-dimensional (3D) X-ray synchrotron tomography
The growth of small corrosion fatigue cracks in alloy 2024
The role of stress-assisted localized corrosion in the development of short fatigue cracks
Journal Article
·
Wed May 14 00:00:00 EDT 2014
· Materials Research Letters
·
OSTI ID:1474321
+3 more
The growth of small corrosion fatigue cracks in alloy 2024
Technical Report
·
Thu Apr 01 00:00:00 EST 1993
·
OSTI ID:1474321
The role of stress-assisted localized corrosion in the development of short fatigue cracks
Conference
·
Mon Dec 01 00:00:00 EST 1997
·
OSTI ID:1474321