Rb based alkali antimonide high quantum efficiency photocathodes for bright electron beam sources and photon detection applications
Journal Article
·
· Journal of Applied Physics
- Cornell Univ., Ithaca, NY (United States). Cornell Lab. for Accelerator-Based Sciences and Education
In this paper, high quantum efficiency alkali antimonide photocathodes have been grown over both stainless steel and glass substrates using sequential evaporation of Sb, K, Rb, and Cs. Quantum efficiencies well above 25% have been measured at 400 nm. Finally, a bi-alkali Rb-K-Sb photocathode grown on a stainless steel substrate has been installed in a high voltage DC gun at Cornell University and the intrinsic electron beam emittance was measured at different photon energies.
- Research Organization:
- Cornell Univ., Ithaca, NY (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES); USDOE Office of Science (SC), High Energy Physics (HEP); National Science Foundation (NSF)
- Grant/Contract Number:
- SC0014338; SC0011643; PHY-1416318
- OSTI ID:
- 1465325
- Alternate ID(s):
- OSTI ID: 1361768
- Journal Information:
- Journal of Applied Physics, Vol. 121, Issue 5; ISSN 0021-8979
- Publisher:
- American Institute of Physics (AIP)Copyright Statement
- Country of Publication:
- United States
- Language:
- English
Cited by: 8 works
Citation information provided by
Web of Science
Web of Science
A cryogenically cooled high voltage DC photoemission electron source
|
journal | August 2018 |
Topological insulators for the generation of electron beams
|
journal | December 2018 |
Similar Records
Direct observation of bi-alkali antimonide photocathodes growth via in operando x-ray diffraction studies
Direct observation of bi-alkali antimonide photocathodes growth via in operando x-ray diffraction studies
Intrinsic emittance reduction in transmission mode photocathodes
Journal Article
·
Mon Dec 01 00:00:00 EST 2014
· APL materials
·
OSTI ID:1465325
+8 more
Direct observation of bi-alkali antimonide photocathodes growth via in operando x-ray diffraction studies
Journal Article
·
Mon Dec 01 00:00:00 EST 2014
· APL Materials
·
OSTI ID:1465325
+9 more
Intrinsic emittance reduction in transmission mode photocathodes
Journal Article
·
Thu Mar 24 00:00:00 EDT 2016
· Applied Physics Letters
·
OSTI ID:1465325