Surface characterization of LaMnO{sub 3+{delta}} powder synthesized using poly(acrylic acid)
Journal Article
·
· Journal of Solid State Chemistry
- Okayama Univ. (Japan)
The La/Mn ratio, specific surface area, and catalytic activity for CO oxidation on perovskite-type LaMnO{sub 3+{delta}} synthesized by firing gels with poly(acrylic acid) (PAA) were measured to characterize the LaMnO{sub 3+{delta}} surface. LaMnO{sub 3+{delta}} synthesized by gel firing with low PAA concentration had a large specific surface area, but a Mn ion content lower than that of LaMnO{sub 3+{delta}} synthesized using acetates. Increasing the PAA concentration or the firing temperature improved the surface state of LaMnO{sub 3+{delta}}. At 5 x 10{sup -2}M PAA, the catalytic activity was better than that of LaMnO{sub 3+{delta}} synthesized using acetates.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 146479
- Journal Information:
- Journal of Solid State Chemistry, Vol. 116, Issue 2; Other Information: PBD: May 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Synthesis of LaMnO{sub 3+{delta}} by firing gels with poly(acrylic acid) in a pure argon stream
Crystal structure of LaMnO[sub 3+[delta]] synthesized using poly(acrylic acid)
Surface characterization of LaMnO{sub 3+{delta}} powder annealed in air
Journal Article
·
Thu Feb 01 00:00:00 EST 1996
· Journal of Solid State Chemistry
·
OSTI ID:146479
Crystal structure of LaMnO[sub 3+[delta]] synthesized using poly(acrylic acid)
Journal Article
·
Tue Jun 01 00:00:00 EDT 1993
· Journal of Solid State Chemistry; (United States)
·
OSTI ID:146479
+1 more
Surface characterization of LaMnO{sub 3+{delta}} powder annealed in air
Journal Article
·
Sun Oct 01 00:00:00 EDT 1995
· Journal of Solid State Chemistry
·
OSTI ID:146479