Polymer blends based on epoxy resin and polyphenylene ether as a matrix material for high-performance composites
- Eindhoven Univ. of Technology (Netherlands). Center for Polymers and Composites
The application of poly(2,6-dimethyl-1,4-phenylene ether), PPE, as a matrix material for continuous carbon fiber reinforced composites was studied. PPE is an amorphous thermoplastic exhibiting a high glass transition temperature (220 C) and outstanding mechanical properties with respect to e.g. toughness. However, due to the limited thermal stability at temperatures above T{sub g}, PPE can be regarded as an intractable polymer. Consequently, the introduction of PPE in a composite structure via a melt impregnation route is not feasible. In this investigation a solution impregnation route, using epoxy resin as a reactive solvent, was developed. During impregnation epoxy resin acts as a solvent which results in enhanced flow and a reduced processing temperature enabling the preparation of high quality composites, avoiding any degradation. Upon curing of the neat system, phase separation and phase inversion occurs resulting in a continuous PPE matrix filled with glassy epoxy spheres. As a result of this morphology the mechanical and thermal properties of the final material are mainly dominated by the PPE component. In composite applications, a strong influence of the polarity of the carbon fiber surface on the resulting matrix morphology was found. Upon curing, phase separation is initiated at the fiber surface resulting in an epoxy `interlayer` at the fiber surface. This phenomenon can provide a high level of interfacial adhesion. A preliminary investigation of the resulting composite materials revealed outstanding mechanical properties with respect to e.g. interlaminar toughness and strength.
- OSTI ID:
- 143630
- Report Number(s):
- CONF-930246-; ISBN 0-87339-251-5; TRN: IM9413%%140
- Resource Relation:
- Conference: Advanced composites `93: international conference on advanced composite materials (ICACM), Wollongong (Australia), 15-19 Feb 1993; Other Information: PBD: 1993; Related Information: Is Part Of Advanced composites 1993; Chandra, T. [ed.] [Univ. of Wollongong (Australia)]; Dhingra, A.K. [ed.] [DuPont, Wilmington, DE (United States)]; PB: 1464 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Morphology development of rubber-modified epoxy thermosets
Model multilayer toughened thermosetting advanced composites