Title: Radiation dose and antioxidant depletion in a HDPE geomembrane

Journal Article · · Geotextiles and Geomembranes
; ; ;

The impact of α and β radiation on antioxidant depletion in smooth high-density polyethylene (HDPE) geo-membranes (GMs) is described. Smooth HDPE GMs having different thickness (0.04-mm, 0.1-mm, 0.2-mm) were created by mechanically pulverizing sections of 2-mm-thick smooth HDPE GM and extruding the polymer at different thicknesses using a film blowing machine. The 2-mm-thick smooth HDPE GM was also used in the experiments. HDPE GM specimens were exposed to sealed sources of 241Am and 99Tc for 1–50 h to simulate the impact of α and β radiation from U and 99Tc in low-level radioactive waste (LLW) leachate. Standard oxidative induction time (OIT) tests were conducted to determine antioxidant depletion. No change in OIT occurred in the 2-mm-thick HDPE GM after exposure to sealed sources of 241Am and 99Tc for 50 h. In much thinner GMs (e.g., 0.04 mm), however, significant antioxidant depletion occurred after exposure most likely due to penetration of α and β particles. Penetration depth of α and β particles and dose deposition in HDPE GMs were estimated with the GEometry ANd Tracking (GEANT4) program. Predictions from GEANT4 show that maximum dose deposition occurs at the surface of the HDPE GM and decreases with depth. A multilayer model is used to estimate anti-oxidant depletion in HDPE GMs for depth-dependent doses. These estimates suggest that radiation from LLW leachate has an insignificant effect on antioxidant depletion in HDPE GMs due to the low dose deposition (e.g., 2.42 Gy) expected over a 1000-yr service life, even if the level of activity in LLW leachate increases 10x to 100x the level typical of today.

Research Organization:
Vanderbilt Univ., Nashville, TN (United States)
Sponsoring Organization:
USDOE
Grant/Contract Number:
FC01-06EW07053
OSTI ID:
1431145
Alternate ID(s):
OSTI ID: 1511035
Journal Information:
Geotextiles and Geomembranes, Journal Name: Geotextiles and Geomembranes Vol. 46 Journal Issue: 4; ISSN 0266-1144
Publisher:
ElsevierCopyright Statement
Country of Publication:
United Kingdom
Language:
English
Citation Metrics:
Cited by: 11 works
Citation information provided by
Web of Science

Figures / Tables (13)

Table 1(p. 2)table Table 1
Fig. 1(p. 3)figure Fig. 1
Fig. 2(p. 4)figure Fig. 2
Fig. 3(p. 5)figure Fig. 3
Fig. 4(p. 5)figure Fig. 4
Fig. 5(p. 6)figure Fig. 5
Fig. 6(p. 6)figure Fig. 6
Fig. 7(p. 7)figure Fig. 7
Fig. 8(p. 7)figure Fig. 8
Fig. 9(p. 7)figure Fig. 9
Fig. 10(p. 8)figure Fig. 10
Fig. A1(p. 9)figure Fig. A1
Fig. A2(p. 10)figure Fig. A2

Similar Records

Related Subjects

42 ENGINEERING
HDPE geomembrane
Antioxidant depletion
Low-level radioactive waste
Radiation
Dose deposition
Service life