Title: Enhanced dielectric properties due to space charge-induced interfacial polarization in multilayer polymer films

Abstract

We report that with the recent advancement of power electronics, polymer film capacitors have become increasingly important. However, the low temperature rating (up to 85 °C) and low energy density (5 J cm -3 at breakdown) of state-of-the-art biaxially oriented polypropylene (BOPP) films have been limiting factors for advanced power electronics. Based on our recent work, multilayer films (MLFs), which consist of a high energy density polymer [e.g., poly(vinylidene fluoride) (PVDF)] and a high breakdown/low loss polymer [e.g., polycarbonate (PC)], have shown potential to achieve high energy density (13–17 J cm -3), enhanced breakdown strength, high temperature tolerance, and low loss simultaneously. In this study, the dielectric properties of PC/PVDF 50/50 32- and 256-layer (32L and 256L) films were investigated. The breakdown strength of the 32L film was as high as 800 MV m -1 at room temperature, as compared to 600 MV m -1 of PVDF and 750 MV m-1 of PC. The temperature rating of the 32L film reached 120 °C, higher than that of BOPP. In addition, it was observed that the 32L film with thicker PC layers exhibited a higher breakdown strength and a lower DC conductivity than the 256L film with thinner PC layers atmore » elevated temperatures. These differences were attributed to the difference in the interfacial polarization of space charges, which was further verified by thermally stimulated depolarization current spectroscopy. In conclusion, we conclude that interfacial polarization endows MLFs with the desirable dielectric properties for next generation film capacitors.« less

Authors:
 [1];  [1];  [1];  [1];  [1];  [2];  [2];  [1]; ORCiD logo [1]
  1. Case Western Reserve Univ., Cleveland, OH (United States). Center for Layered Polymeric Systems (CLiPS) and Department of Macromolecular Science and Engineering
  2. Brookhaven National Lab. (BNL), Upton, NY (United States). National Synchrotron Light Source II (NSLS-II)
Publication Date:
Research Org.:
Brookhaven National Lab. (BNL), Upton, NY (United States)
Sponsoring Org.:
USDOE Office of Science (SC), Basic Energy Sciences (BES)
OSTI Identifier:
1430873
Report Number(s):
BNL-203427-2018-JAAM
Journal ID: ISSN 2050-7526; JMCCCX; TRN: US1802925
Grant/Contract Number:  
SC0012704
Resource Type:
Journal Article: Accepted Manuscript
Journal Name:
Journal of Materials Chemistry C
Additional Journal Information:
Journal Volume: 5; Journal Issue: 39; Journal ID: ISSN 2050-7526
Publisher:
Royal Society of Chemistry
Country of Publication:
United States
Language:
English
Subject:
36 MATERIALS SCIENCE

Citation Formats

Chen, Xinyue, Tseng, Jung-Kai, Treufeld, Imre, Mackey, Matthew, Schuele, Donald E., Li, Ruipeng, Fukuto, Masafumi, Baer, Eric, and Zhu, Lei. Enhanced dielectric properties due to space charge-induced interfacial polarization in multilayer polymer films. United States: N. p., 2017. Web. doi:10.1039/C7TC03653A.
Chen, Xinyue, Tseng, Jung-Kai, Treufeld, Imre, Mackey, Matthew, Schuele, Donald E., Li, Ruipeng, Fukuto, Masafumi, Baer, Eric, & Zhu, Lei. Enhanced dielectric properties due to space charge-induced interfacial polarization in multilayer polymer films. United States. https://doi.org/10.1039/C7TC03653A
Chen, Xinyue, Tseng, Jung-Kai, Treufeld, Imre, Mackey, Matthew, Schuele, Donald E., Li, Ruipeng, Fukuto, Masafumi, Baer, Eric, and Zhu, Lei. Fri . "Enhanced dielectric properties due to space charge-induced interfacial polarization in multilayer polymer films". United States. https://doi.org/10.1039/C7TC03653A. https://www.osti.gov/servlets/purl/1430873.
@article{osti_1430873,
title = {Enhanced dielectric properties due to space charge-induced interfacial polarization in multilayer polymer films},
author = {Chen, Xinyue and Tseng, Jung-Kai and Treufeld, Imre and Mackey, Matthew and Schuele, Donald E. and Li, Ruipeng and Fukuto, Masafumi and Baer, Eric and Zhu, Lei},
abstractNote = {We report that with the recent advancement of power electronics, polymer film capacitors have become increasingly important. However, the low temperature rating (up to 85 °C) and low energy density (5 J cm-3 at breakdown) of state-of-the-art biaxially oriented polypropylene (BOPP) films have been limiting factors for advanced power electronics. Based on our recent work, multilayer films (MLFs), which consist of a high energy density polymer [e.g., poly(vinylidene fluoride) (PVDF)] and a high breakdown/low loss polymer [e.g., polycarbonate (PC)], have shown potential to achieve high energy density (13–17 J cm-3), enhanced breakdown strength, high temperature tolerance, and low loss simultaneously. In this study, the dielectric properties of PC/PVDF 50/50 32- and 256-layer (32L and 256L) films were investigated. The breakdown strength of the 32L film was as high as 800 MV m-1 at room temperature, as compared to 600 MV m-1 of PVDF and 750 MV m-1 of PC. The temperature rating of the 32L film reached 120 °C, higher than that of BOPP. In addition, it was observed that the 32L film with thicker PC layers exhibited a higher breakdown strength and a lower DC conductivity than the 256L film with thinner PC layers at elevated temperatures. These differences were attributed to the difference in the interfacial polarization of space charges, which was further verified by thermally stimulated depolarization current spectroscopy. In conclusion, we conclude that interfacial polarization endows MLFs with the desirable dielectric properties for next generation film capacitors.},
doi = {10.1039/C7TC03653A},
url = {https://www.osti.gov/biblio/1430873}, journal = {Journal of Materials Chemistry C},
issn = {2050-7526},
number = 39,
volume = 5,
place = {United States},
year = {2017},
month = {9}
}

Journal Article:
Free Publicly Available Full Text
Publisher's Version of Record

Citation Metrics:
Cited by: 6 works
Citation information provided by
Web of Science

Save / Share:

Works referenced in this record:

Capacitors: operating principles, current market and technical trends
journal, June 1996


Layer confinement effect on charge migration in polycarbonate/poly(vinylidene fluorid- co -hexafluoropropylene) multilayered films
journal, June 2012


Capacitive components for power electronics
journal, June 2001


Interfacial Polarization-Induced Loss Mechanisms in Polypropylene/BaTiO 3 Nanocomposite Dielectrics
journal, June 2016


Multilayered polycarbonate/poly(vinylidene fluoride-co-hexafluoropropylene) for high energy density capacitors with enhanced lifetime
journal, May 2012


Polymer nanocomposite dielectrics - the role of the interface
journal, August 2005


Copolymerization of fluorinated monomers: recent developments and future trends
journal, June 2000


Reduction of Dielectric Hysteresis in Multilayered Films via Nanoconfinement
journal, February 2012


Effect of biaxial orientation on dielectric and breakdown properties of poly(ethylene terephthalate)/poly(vinylidene fluoride- co -tetrafluoroethylene) multilayer films
journal, March 2013


Numerical analysis of electrical response: Statics and dynamics of space‐charge regions at blocking electrodes
journal, January 1979


Analysis and Evaluation of DC-Link Capacitors for High-Power-Density Electric Vehicle Drive Systems
journal, September 2012


Polymer nanocomposites for electrical energy storage
journal, August 2011


Dielectric breakdown of polyvinylidene fluoride and its comparisons with other polymers
journal, May 1993


Polymer-Based Dielectrics with High Energy Storage Density
journal, July 2015


High field conduction in biaxially oriented polypropylene at elevated temperature
journal, June 2012


Exploring Strategies for High Dielectric Constant and Low Loss Polymer Dielectrics
journal, October 2014


Enhanced breakdown strength of multilayered films fabricated by forced assembly microlayer coextrusion
journal, August 2009


The mechanisms leading to the useful electrical properties of polymer nanodielectrics
journal, January 2008


Capacitors
journal, January 1990


Capacitors
journal, January 1998


Ferroelectric Polymers
journal, June 1983


Confined crystallization of PVDF and a PVDF-TFE copolymer in nanolayered films
journal, October 2011


    Works referencing / citing this record:

    Polymer multilayer films for high temperature capacitor application
    journal, January 2019


    Deformation and failure of polycarbonate in an electric field
    journal, August 2019


    Tough thermosetting polyurethanes and adhesives from rubber seed oil by hydroformylation
    journal, September 2019


    Sn‐Polyester/Polyimide Hybrid Flexible Free‐Standing Film as a Tunable Dielectric Material
    journal, November 2018


    Multilayered hierarchical polymer composites for high energydensity capacitors
    journal, January 2019


    Interface design for high energy density polymer nanocomposites
    journal, January 2019


    Reducing leakage current and dielectric losses of electroactive polymers through electro-annealing for high-voltage actuation
    journal, January 2019


    Multilayer-structured transparent MXene/PVDF film with excellent dielectric and energy storage performance
    journal, January 2019