Decomposition of silicon carbide at high pressures and temperatures
We measure the onset of decomposition of silicon carbide, SiC, to silicon and carbon (e.g., diamond) at high pressures and high temperatures in a laser-heated diamond-anvil cell. We identify decomposition through x-ray diffraction and multiwavelength imaging radiometry coupled with electron microscopy analyses on quenched samples. We find that B3 SiC (also known as 3C or zinc blende SiC) decomposes at high pressures and high temperatures, following a phase boundary with a negative slope. The high-pressure decomposition temperatures measured are considerably lower than those at ambient, with our measurements indicating that SiC begins to decompose at ~ 2000 K at 60 GPa as compared to ~ 2800 K at ambient pressure. Once B3 SiC transitions to the high-pressure B1 (rocksalt) structure, we no longer observe decomposition, despite heating to temperatures in excess of ~ 3200 K. The temperature of decomposition and the nature of the decomposition phase boundary appear to be strongly influenced by the pressure-induced phase transitions to higher-density structures in SiC, silicon, and carbon. The decomposition of SiC at high pressure and temperature has implications for the stability of naturally forming moissanite on Earth and in carbon-rich exoplanets.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- OSTI ID:
- 1417379
- Journal Information:
- Physical Review B, Vol. 96, Issue 17; ISSN 2469-9950
- Publisher:
- American Physical Society (APS)
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
SILICON CARBIDE CERAMICS FOR COMPACT HEAT EXCHANGERS
Isothermal Martensitic and Pressure-Induced Delta to Alpha-Prime Phase Transformations in a Pu-Ga Alloy