An analysis of premature cracking associated with microstructural alterations in an AISI 52100 failed wind turbine bearing using X-ray tomography
Crack surrounded by local areas of microstructural alteration deemed "White etching cracks" (WECs) lead to unpredictable and premature failures within a multitude of applications including wind turbine gearbox bearings. While the exact cause of these failures remains unknown, a large number of hypotheses exist as to how and why these cracks form. The aim of the current work is to elucidate some of these hypotheses by mapping WEC networks within failed wind turbine bearings using high energy X-ray tomography, in an attempt to determine the location of WEC initiation, and the role of defects within the steel, such as inclusions or carbide clusters. Four completely subsurface WECs were found throughout the presented analysis, thereby confirming subsurface initiation as method of WEC formation. Additionally, a multitude of small butterfly like cracks were found around inclusions in the steel, however further analysis is needed to verify if these inclusions are initiation sites for WECs. (C) 2017 Elsevier Ltd. All rights reserved.
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE) - Wind and Water Power Technolgoies (WWPTO)
- DOE Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1411157
- Journal Information:
- Materials & Design, Vol. 117, Issue C; ISSN 0264-1275
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
Similar Records
The influence of steel microstructure and inclusion characteristics on the formation of premature bearing failures with microstructural alterations
Effect of Retained Austininte on White Etching Crack Behavior of Carburized AISI 8620 Steel Under Boundary Lubrication