Phase transformation kinetics in rolled U-10 wt. % Mo foil: Effect of post-rolling heat treatment and prior γ-UMo grain size
The effect of sub-eutectoid heat treatment on the phase transformation behavior in rolled U-10 wt.percent Mo (U10Mo) foils was systematically investigated. The as-cast 5 mm thick foils were initially homogenized at 900 degrees C for 48 hours and were hot rolled to 2 mm and later cold rolled down to 0.2 mm. Three starting microstructures were evaluated: (i) hot- + cold-rolled to 0.2 mm (as-rolled condition), (ii) hot- + cold-rolled to 0.2 mm + annealed at 700 deg. C for 1 hour, and (iii) hot- + cold-rolled to 0.2 mm + annealed at 1000 deg. C for 60 hours. U10Mo rolled foils went through various degrees of decomposition when subjected to the sub-eutectoid heat-treatment step and formed a lamellar microstructure through a cellular reaction mostly along the previous γ-UMo grain boundaries.
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1406704
- Report Number(s):
- PNNL-SA-127108; DN2006000
- Journal Information:
- Journal of Nuclear Materials, Vol. 496, Issue C; ISSN 0022-3115
- Publisher:
- Elsevier
- Country of Publication:
- United States
- Language:
- English
Preparation of γ-Uranium-Molybdenum Alloys by Electrochemical Reduction of Solid Oxides in LiCl Molten Salt
|
journal | January 2019 |
Discontinuous Precipitation in U-10 wt.%Mo Alloy: Reaction Kinetics, Effect of Prior γ-UMo Microstructure, the Role of Grain-Boundary Misorientation, and the Effect of Ternary Alloying Addition
|
journal | June 2019 |
Texture Evolution in U-10Mo Nuclear Fuel Foils during Plasma Spray Coating with Zr
|
journal | May 2018 |
Similar Records
Discontinuous Precipitation in U-10 wt.%Mo Alloy: Reaction Kinetics, Effect of Prior gamma-UMo Microstructure, the Role of Grain-Boundary Misorientation, and the Effect of Ternary Alloying Addition
The Effect of Rolling As-Cast and Homogenized U-10Mo Samples on the Microstructure Development and Recovery Curves