Title: Stress intensity factor solutions for welds in lap-shear specimens of dissimilar sheet materials with and without kinked cracks

Journal Article · · Engineering Fracture Mechanics
;

Sponsoring Organization:
USDOE Office of Energy Efficiency and Renewable Energy (EERE)
OSTI ID:
1396586
Journal Information:
Engineering Fracture Mechanics, Journal Name: Engineering Fracture Mechanics Vol. 177 Journal Issue: C; ISSN 0013-7944
Publisher:
ElsevierCopyright Statement
Country of Publication:
United Kingdom
Language:
English
Citation Metrics:
Cited by: 4 works
Citation information provided by
Web of Science

References (24)

Plane Problems of Cracks in Dissimilar Media journal June 1965
Fatigue life estimation of ultrasonic spot welded Mg alloy joints journal October 2014
Joint formation in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds journal August 2009
Comparison of fatigue behavior in Mg/Mg similar and Mg/steel dissimilar refill friction stir spot welds journal November 2016
Modeling of failure mode of laser welds in lap-shear specimens of HSLA steel sheets journal January 2011
Ultrasonic Spot Welding of AZ31B to Galvanized Mild Steel journal April 2010
Hot Cracking of Resistance Spot Welded Magnesium Alloy journal January 2008
Elastic Fracture Mechanics Concepts for Interfacial Cracks journal March 1988
Fatigue behaviour of magnesium to steel dissimilar friction stir lap joints journal February 2012
Slightly curved or kinked cracks journal April 1980
Fatigue behavior of tailor (laser)-welded blanks for automotive applications journal March 2006
Kinking of a Crack Out of an Interface journal June 1989
Failure mode of laser welds in lap-shear specimens of high strength low alloy (HSLA) steel sheets: FAILURE MODE OF LASER WELDS journal August 2011
Ultrasonic spot welded AZ31 magnesium alloy: Microstructure, texture, and lap shear strength journal May 2013
Spot Friction Welding of Aluminum to Steel conference April 2007
Interface crack between two elastic layers journal May 1990
Comparative study of fatigue behaviour in dissimilar Al alloy/steel and Mg alloy/steel friction stir spot welds fabricated by scroll grooved tool without probe journal July 2012
Ultrasonic welding between mild steel sheet and Al–Mg alloy sheet journal August 2009
Stress Distribution in a Nonhomogeneous Elastic Plane With Cracks journal June 1963
Fatigue behavior of laser welds in lap-shear specimens of high strength low alloy steel sheets journal April 2014
Stress intensity factor solutions for estimation of fatigue lives of laser welds in lap-shear specimens journal May 2011
Mechanisms of joint and microstructure formation in high power ultrasonic spot welding 6111 aluminium automotive sheet journal September 2010
The Effect of Anvil Geometry and Welding Energy on Microstructures in Ultrasonic Spot Welds of AA6111-T4 journal April 2007
Welding Characteristics of Aluminum and Copper Plate Specimens Welded by a 19 kHz Complex Vibration Ultrasonic Seam Welding System journal May 2002

Similar Records

Stress intensity factor solutions for adhesive-bonded lap-shear specimens of magnesium and steel sheets with and without kinked cracks for fatigue life estimations
Journal Article · Sat Nov 01 00:00:00 EDT 2014 · Engineering Fracture Mechanics · OSTI ID:1396586
Accurate analytical structural stress and stress intensity factor solutions for similar and dissimilar spot welds in lap-shear specimens
Journal Article · Fri Sep 01 00:00:00 EDT 2017 · Engineering Fracture Mechanics · OSTI ID:1396586
Stress intensity factor solutions for similar and dissimilar spot welds in lap-shear specimens under clamped loading conditions
Journal Article · Thu Jun 01 00:00:00 EDT 2017 · Engineering Fracture Mechanics · OSTI ID:1396586

Related Subjects