Structural Evolution of Reversible Mg Insertion into a Bilayer Structure of V ₂ O ₅ · n H ₂ O Xerogel Material

Journal Article · Tue May 10 00:00:00 EDT 2016 · Chemistry of Materials

DOI:https://doi.org/10.1021/acs.chemmater.6b00026· OSTI ID:1390784

Sa, Niya; Kinnibrugh, Tiffany L.; Wang, Hao; Sai Gautam, Gopalakrishnan; Chapman, Karena W.; Vaughey, John T.; Key, Baris; Fister, Timothy T.; Freeland, John W.; Proffit, Danielle L.; Chupas, Peter J.; Ceder, Gerbrand; Bareno, Javier G.; Bloom, Ira D.; Burrell, Anthony K.

Functional multivalent intercalation cathodes represent one of the largest hurdles in the development of Mg batteries. While there are many reports of Mg cathodes, many times the evidence of intercalation chemistry is only circumstantial. In this work, direct evidence of Mg intercalation into a bilayer structure of V2O5·nH2O xerogel is confirmed, and the nature of the Mg intercalated species is reported. The interlayer spacing of V2O5·nH2O contracts upon Mg intercalation and expands for Mg deintercalation due to the strong electrostatic interaction between the divalent cation and the cathode. A combination of NMR, pair distribution function (PDF) analysis, and X-ray absorption near edge spectroscopy (XANES) confirmed reversible Mg insertion into the V2O5·nH2O material, and structural evolution of Mg intercalation leads to the formation of multiple new phases. Structures of V2O5·nH2O with Mg intercalation were further supported by the first principle simulations. A solvent cointercalated Mg in V2O5·nH2O is observed for the first time, and the 25Mg magic angle spinning nuclear magnetic resonance (MAS NMR) spectroscopy was used to elucidate the structure obtained upon electrochemical cycling. Specifically, existence of a well-defined Mg–O environment is revealed for the Mg intercalated structures. Information reported here reveals the fundamental Mg ion intercalation mechanism in a bilayer structure of V2O5·nH2O material and provides insightful design metrics for future Mg cathodes.

• Research Organization: Argonne National Lab. (ANL), Argonne, IL (United States)
• Sponsoring Organization: USDOE Office of Science (SC), Basic Energy Sciences (BES)
• DOE Contract Number: AC02-06CH11357
• OSTI ID: 1390784
• Journal Information: Chemistry of Materials, Vol. 28, Issue 9; ISSN 0897-4756
• Publisher: American Chemical Society (ACS)
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE