Comparing Matched Polymer:Fullerene Solar Cells Made by Solution-Sequential Processing and Traditional Blend Casting: Nanoscale Structure and Device Performance
Journal Article
·
· Journal of Physical Chemistry. C
- Materials Measurement Science Division, Material Measurement Laboratory, National Institute of Standards and Technology, Gaithersburg, Maryland 20899, United States
- California NanoSystems Institute, University of California, Los Angeles, Los Angeles, California 90095, United States
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Molecularly Engineered Energy Materials (MEEM)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- SC0001342
- OSTI ID:
- 1384401
- Journal Information:
- Journal of Physical Chemistry. C, Vol. 118, Issue 31; Related Information: MEEM partners with University of California, Los Angeles (lead); University of California, Berkeley; Eastern Washington University; University of Kansas; National Renewable Energy Laboratory; ISSN 1932-7447
- Publisher:
- American Chemical Society
- Country of Publication:
- United States
- Language:
- English
Similar Records
Comparing Matched Polymer:Fullerene Solar Cells Made by Solution- Sequential Processing and Traditional Blend Casting: Nanoscale Structure and Device Performance
Crystallinity Effects in Sequentially Processed and Blend-Cast Bulk-Heterojunction Polymer/Fullerene Photovoltaics
Crystallinity Effects in Sequentially Processed and Blend-Cast Bulk- Heterojunction Polymer/Fullerene Photovoltaics
Journal Article
·
Thu Aug 07 00:00:00 EDT 2014
· Journal of Physical Chemistry C
·
OSTI ID:1384401
+7 more
Crystallinity Effects in Sequentially Processed and Blend-Cast Bulk-Heterojunction Polymer/Fullerene Photovoltaics
Journal Article
·
Wed Jul 30 00:00:00 EDT 2014
· Journal of Physical Chemistry. C
·
OSTI ID:1384401
+4 more
Crystallinity Effects in Sequentially Processed and Blend-Cast Bulk- Heterojunction Polymer/Fullerene Photovoltaics
Journal Article
·
Thu Aug 14 00:00:00 EDT 2014
· Journal of Physical Chemistry C
·
OSTI ID:1384401
+4 more