Adhesion of Antireflective Coatings in Multijunction Photovoltaics
The development of a new composite dual cantilever beam (cDCB) thin-film adhesion testing method is reported, which allows the measurement of adhesion on the fragile thin substrates used in multijunction photovoltaics. We address the adhesion of several antireflective coating systems on multijunction cells. By varying interface chemistry and morphology, we demonstrate the ensuing effects on adhesion and help to develop an understanding of how high adhesion can be achieved, as adhesion values ranging from 0.5 J/m2 to 10 J/m2 were measured. Damp Heat (85 degrees C/85% RH) was used to invoke degradation of interfacial adhesion. We show that even with germanium substrates that fracture easily, quantitative measurements of adhesion can still be made at high test yield. The cDCB test is discussed as an important new methodology, which can be broadly applied to any system that makes use of thin, brittle, or otherwise fragile substrates.
- Research Organization:
- National Renewable Energy Lab. (NREL), Golden, CO (United States)
- Sponsoring Organization:
- USDOE Office of Energy Efficiency and Renewable Energy (EERE)
- DOE Contract Number:
- AC36-08GO28308
- OSTI ID:
- 1343400
- Report Number(s):
- NREL/CP-5J00-67922
- Resource Relation:
- Conference: Presented at the 2016 IEEE 43rd Photovoltaic Specialists Conference (PVSC), 5-10 June 2016, Portland, Oregon
- Country of Publication:
- United States
- Language:
- English
Similar Records
Quantitative adhesion characterization of antireflective coatings in multijunction photovoltaics
Studying the Formation of Antireflection Coatings on Multijunction Solar Cells