Irradiation-induced effects of proton irradiation on zirconium carbides with different stoichiometries
Zirconium carbide (ZrC) is being considered for utilization in deep burn TRISO fuel particles for hightemperature, gas-cooled reactors. Zirconium carbide has a cubic B1 type crystal structure along with a very high melting point (3420 ?C), exceptional hardness and good thermal and electrical conductivities. Understanding the ZrC irradiation response is crucial for establishing ZrC as an alternative component in TRISO fuel. Until now, very few studies on irradiation effects on ZrC have been released and fundamental aspects of defect evolution and kinetics are not well understood although some atomistic simulations and phenomenological studies have been performed. This work was carried out to understand the damage evolution in float-zone refined ZrC with different stoichiometries. Proton irradiations at 800 ?C up to doses of 3 dpa were performed on ZrCx (where x ranges from 0.9 to 1.2) to investigate the damage evolution. The irradiation-induced defects, such as density of dislocation loops, at different stoichiometries and doses which were characterized by transmission electron microscopy (TEM) is presented and discussed.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- DOE - NE
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 1162221
- Report Number(s):
- INL/JOU-14-33533
- Journal Information:
- Nuclear Engineering and Design, Vol. 227; ISSN 0029-5493
- Country of Publication:
- United States
- Language:
- English
Similar Records
Swift heavy ion irradiation effects in zirconium and hafnium carbides
Pre- and post-irradiation characterization and properties measurements of ZrC coated surrogate TRISO particles