Title: High-Temperature Thermoelectric Properties of the Solid-Solution Zintl Phase Eu 11Cd 6Sb 12-xAs x (x < 3)

Abstract

Zintl phases are compounds that have shown promise for thermoelectric applications. The title solid–solution Zintl compounds were prepared from the elements as single crystals using a tin flux for compositions x = 0, 1, 2, and 3. Eu 11Cd 6Sb 12–xAs x (x < 3) crystallize isostructurally in the centrosymmetric monoclinic space group C2/m (no. 12, Z = 2) as the Sr 11Cd 6Sb 12 structure type (Pearson symbol mC58). Efforts to make the As compositions for x exceeding ~3 resulted in structures other than the Sr 11Cd 6Sb 12 structure type. Single-crystal X-ray diffraction indicates that As does not randomly substitute for Sb in the structure but is site specific for each composition. The amount of As determined by structural refinement was verified by electron microprobe analysis. Electronic structures and energies calculated for various model structures of Eu 11Cd 6Sb 10As 2 (x = 2) indicated that the preferred As substitution pattern involves a mixture of three of the six pnicogen sites in the asymmetric unit. In addition, As substitution at the Pn4 site opens an energy gap at the Fermi level, whereas substitution at the other five pnicogen sites remains semimetallic with a pseudo gap. Thermoelectric properties ofmore » these compounds were measured on hot-pressed, fully densified pellets. Samples show exceptionally low lattice thermal conductivities from room temperature to 775 K: 0.78–0.49 W/mK for x = 0; 0.72–0.53 W/mK for x = 1; and 0.70–0.56 W/mK for x = 2. Eu 11Cd 6Sb 12 shows a high p-type Seebeck coefficient (from +118 to 153 μ V/K) but also high electrical resistivity (6.8 to 12.8 mΩ·cm). The value of zT reaches 0.23 at 774 K. The properties of Eu 11Cd 6Sb 12–xAs x are interpreted in discussion with the As site substitution.« less

Authors:
; ; ; ; ; ;  [1];  [2];  [2]
  1. CIT
  2. (
Publication Date:
Research Org.:
Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
Sponsoring Org.:
NSFOTHER
OSTI Identifier:
1121453
Resource Type:
Journal Article
Resource Relation:
Journal Name: Chemistry of Materials; Journal Volume: 26; Journal Issue: 3
Country of Publication:
United States
Language:
ENGLISH

Citation Formats

Kazem, Nasrin, Xie, Weiwei, Ohno, Saneyuki, Zevalkink, Alexandra, Miller, Gordon J., Snyder, G. Jeffrey, Kauzlarich, Susan M., UCD), and Iowa State). High-Temperature Thermoelectric Properties of the Solid-Solution Zintl Phase Eu11Cd6Sb12-xAsx (x < 3). United States: N. p., 2014. Web. doi:10.1021/cm403345a.
Kazem, Nasrin, Xie, Weiwei, Ohno, Saneyuki, Zevalkink, Alexandra, Miller, Gordon J., Snyder, G. Jeffrey, Kauzlarich, Susan M., UCD), & Iowa State). High-Temperature Thermoelectric Properties of the Solid-Solution Zintl Phase Eu11Cd6Sb12-xAsx (x < 3). United States. doi:10.1021/cm403345a.
Kazem, Nasrin, Xie, Weiwei, Ohno, Saneyuki, Zevalkink, Alexandra, Miller, Gordon J., Snyder, G. Jeffrey, Kauzlarich, Susan M., UCD), and Iowa State). Thu . "High-Temperature Thermoelectric Properties of the Solid-Solution Zintl Phase Eu11Cd6Sb12-xAsx (x < 3)". United States. doi:10.1021/cm403345a.
@article{osti_1121453,
title = {High-Temperature Thermoelectric Properties of the Solid-Solution Zintl Phase Eu11Cd6Sb12-xAsx (x < 3)},
author = {Kazem, Nasrin and Xie, Weiwei and Ohno, Saneyuki and Zevalkink, Alexandra and Miller, Gordon J. and Snyder, G. Jeffrey and Kauzlarich, Susan M. and UCD) and Iowa State)},
abstractNote = {Zintl phases are compounds that have shown promise for thermoelectric applications. The title solid–solution Zintl compounds were prepared from the elements as single crystals using a tin flux for compositions x = 0, 1, 2, and 3. Eu11Cd6Sb12–xAsx (x < 3) crystallize isostructurally in the centrosymmetric monoclinic space group C2/m (no. 12, Z = 2) as the Sr11Cd6Sb12 structure type (Pearson symbol mC58). Efforts to make the As compositions for x exceeding ~3 resulted in structures other than the Sr11Cd6Sb12 structure type. Single-crystal X-ray diffraction indicates that As does not randomly substitute for Sb in the structure but is site specific for each composition. The amount of As determined by structural refinement was verified by electron microprobe analysis. Electronic structures and energies calculated for various model structures of Eu11Cd6Sb10As2 (x = 2) indicated that the preferred As substitution pattern involves a mixture of three of the six pnicogen sites in the asymmetric unit. In addition, As substitution at the Pn4 site opens an energy gap at the Fermi level, whereas substitution at the other five pnicogen sites remains semimetallic with a pseudo gap. Thermoelectric properties of these compounds were measured on hot-pressed, fully densified pellets. Samples show exceptionally low lattice thermal conductivities from room temperature to 775 K: 0.78–0.49 W/mK for x = 0; 0.72–0.53 W/mK for x = 1; and 0.70–0.56 W/mK for x = 2. Eu11Cd6Sb12 shows a high p-type Seebeck coefficient (from +118 to 153 μ V/K) but also high electrical resistivity (6.8 to 12.8 mΩ·cm). The value of zT reaches 0.23 at 774 K. The properties of Eu11Cd6Sb12–xAsx are interpreted in discussion with the As site substitution.},
doi = {10.1021/cm403345a},
journal = {Chemistry of Materials},
number = 3,
volume = 26,
place = {United States},
year = {Thu Feb 20 00:00:00 EST 2014},
month = {Thu Feb 20 00:00:00 EST 2014}
}