Development of a new casting method to fabricate U–Zr alloy containing minor actinides
Metal fuel slugs of U–Zr alloys for a sodium-cooled fast reactor (SFR) have conventionally been fabricated using an injection casting method. However, casting alloys containing volatile radioactive constituents, such as Am, are problematic in a conventional injection casting method. As an alternative fabrication method, low pressure gravity casting has been developed. Casting soundness, microstructural characteristics, alloying composition, density, and fuel losses were evaluated for the following as-cast fuel slugs: U–10 wt% Zr, U–10 wt% Zr–5 wt% RE, and U–10 wt% Zr–5 wt% RE–5 wt% Mn. The U and Zr contents were uniform throughout the matrix, and impurities such as oxyen, carbon, and nitrogen satisfied the specification of total impurities less than 2,000 ppm. The appearance of the fuel slugs was generally sound, and the internal integrity was shown to be satisfactory based on gamma-ray radiography. In a volatile surrogate casting test, the U–Zr–RE–Mn fuel slug showed that nearly all of the manganese was retained when casting was done under an inert atmosphere.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 1121356
- Report Number(s):
- INL/JOU-14-31373
- Journal Information:
- Journal of Radioanalytical and Nuclear Chemistry, Vol. 299, Issue 1
- Country of Publication:
- United States
- Language:
- English
Similar Records
Microstructural Characteristics of U-Zr Ingot Slug and Atomized Powder for SFR metal Fuel
Alternative Fabrication of Volatile Metal Fuel Slugs for Sodium-cooled Fast Reactor