Title: ALD of Al2O3 for Highly Improved Performance in Li-Ion Batteries

Abstract

Significant advances in energy density, rate capability and safety will be required for the implementation of Li-ion batteries in next generation electric vehicles. We have demonstrated atomic layer deposition (ALD) as a promising method to enable superior cycling performance for a vast variety of battery electrodes. The electrodes range from already demonstrated commercial technologies (cycled under extreme conditions) to new materials that could eventually lead to batteries with higher energy densities. For example, an Al2O3 ALD coating with a thickness of ~ 8 A was able to stabilize the cycling of unexplored MoO3 nanoparticle anodes with a high volume expansion. The ALD coating enabled stable cycling at C/2 with a capacity of ~ 900 mAh/g. Furthermore, rate capability studies showed the ALD-coated electrode maintained a capacity of 600 mAh/g at 5C. For uncoated electrodes it was only possible to observe stable cycling at C/10. Also, we recently reported that a thin ALD Al2O3 coating with a thickness of ~5 A can enable natural graphite (NG) electrodes to exhibit remarkably durable cycling at 50 degrees C. The ALD-coated NG electrodes displayed a 98% capacity retention after 200 charge-discharge cycles. In contrast, bare NG showed a rapid decay. Additionally, Al2O3 ALD filmsmore » with a thickness of 2 to 4 A have been shown to allow LiCoO2 to exhibit 89% capacity retention after 120 charge-discharge cycles performed up to 4.5 V vs Li/Li+. Bare LiCoO2 rapidly deteriorated in the first few cycles. The capacity fade is likely caused by oxidative decomposition of the electrolyte at higher potentials or perhaps cobalt dissolution. Interestingly, we have recently fabricated full cells of NG and LiCoO2 where we coated both electrodes, one or the other electrode as well as neither electrode. In creating these full cells, we observed some surprising results that lead us to obtain a greater understanding of the ALD coatings. We have also recently coated a binder free LiNi0.04Mn0.04Co02O2 electrode containing 5 wt% single-walled carbon nanotubes as the conductive additive and demonstrated both high rate capability as well as the ability to cycle the cathode to 5 V vrs. Li/Li+. Finally, we coated a Celgard (TM) separator and enabled stable cycling in a high dielectric electrolyte. These results will be presented in detail.« less

Authors:
; ; ; ; ; ; ;
Publication Date:
Research Org.:
National Renewable Energy Lab. (NREL), Golden, CO (United States)
Sponsoring Org.:
USDOE Office of Science, Basic Energy Sciences
OSTI Identifier:
1087222
DOE Contract Number:  
AC36-08GO28308
Resource Type:
Conference
Resource Relation:
Conference: American Chemical Society. Abstracts of Papers of the 244th ACS National Meeting, 19-23 August 2012, Philadelphia, Pennsylvania; Related Information: Abstract No. ENFL-661
Country of Publication:
United States
Language:
English
Subject:
25 ENERGY STORAGE; Chemical and Material Sciences

Citation Formats

Dillon, A., Jung, Y. S., Ban, C., Riley, L., Cavanagh, A., Yan, Y., George, S., and Lee, S. H. ALD of Al2O3 for Highly Improved Performance in Li-Ion Batteries. United States: N. p., 2012. Web.
Dillon, A., Jung, Y. S., Ban, C., Riley, L., Cavanagh, A., Yan, Y., George, S., & Lee, S. H. ALD of Al2O3 for Highly Improved Performance in Li-Ion Batteries. United States.
Dillon, A., Jung, Y. S., Ban, C., Riley, L., Cavanagh, A., Yan, Y., George, S., and Lee, S. H. Sun . "ALD of Al2O3 for Highly Improved Performance in Li-Ion Batteries". United States.
@article{osti_1087222,
title = {ALD of Al2O3 for Highly Improved Performance in Li-Ion Batteries},
author = {Dillon, A. and Jung, Y. S. and Ban, C. and Riley, L. and Cavanagh, A. and Yan, Y. and George, S. and Lee, S. H.},
abstractNote = {Significant advances in energy density, rate capability and safety will be required for the implementation of Li-ion batteries in next generation electric vehicles. We have demonstrated atomic layer deposition (ALD) as a promising method to enable superior cycling performance for a vast variety of battery electrodes. The electrodes range from already demonstrated commercial technologies (cycled under extreme conditions) to new materials that could eventually lead to batteries with higher energy densities. For example, an Al2O3 ALD coating with a thickness of ~ 8 A was able to stabilize the cycling of unexplored MoO3 nanoparticle anodes with a high volume expansion. The ALD coating enabled stable cycling at C/2 with a capacity of ~ 900 mAh/g. Furthermore, rate capability studies showed the ALD-coated electrode maintained a capacity of 600 mAh/g at 5C. For uncoated electrodes it was only possible to observe stable cycling at C/10. Also, we recently reported that a thin ALD Al2O3 coating with a thickness of ~5 A can enable natural graphite (NG) electrodes to exhibit remarkably durable cycling at 50 degrees C. The ALD-coated NG electrodes displayed a 98% capacity retention after 200 charge-discharge cycles. In contrast, bare NG showed a rapid decay. Additionally, Al2O3 ALD films with a thickness of 2 to 4 A have been shown to allow LiCoO2 to exhibit 89% capacity retention after 120 charge-discharge cycles performed up to 4.5 V vs Li/Li+. Bare LiCoO2 rapidly deteriorated in the first few cycles. The capacity fade is likely caused by oxidative decomposition of the electrolyte at higher potentials or perhaps cobalt dissolution. Interestingly, we have recently fabricated full cells of NG and LiCoO2 where we coated both electrodes, one or the other electrode as well as neither electrode. In creating these full cells, we observed some surprising results that lead us to obtain a greater understanding of the ALD coatings. We have also recently coated a binder free LiNi0.04Mn0.04Co02O2 electrode containing 5 wt% single-walled carbon nanotubes as the conductive additive and demonstrated both high rate capability as well as the ability to cycle the cathode to 5 V vrs. Li/Li+. Finally, we coated a Celgard (TM) separator and enabled stable cycling in a high dielectric electrolyte. These results will be presented in detail.},
doi = {},
journal = {},
number = ,
volume = ,
place = {United States},
year = {2012},
month = {1}
}

Conference:
Other availability
Please see Document Availability for additional information on obtaining the full-text document. Library patrons may search WorldCat to identify libraries that hold this conference proceeding.

Save / Share: