A comparison of texture results obtained using neutron and ASTAR methods at diminishing length scales in ordered metallic nanolamellar composites
Journal Article
·
· Scripta Materialia
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Center for Materials at Irradiation and Mechanical Extremes (CMIME)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- 2008LANL1026
- OSTI ID:
- 1067130
- Journal Information:
- Scripta Materialia, Vol. 67, Issue 4; Related Information: CMIME partners with Los Alamos National Laboratory (lead); Carnegie Mellon University; University of Illinois, Urbana Champaign; Massachusetts Institute of Technology; University of Nebraska; ISSN 1359-6462
- Country of Publication:
- United States
- Language:
- English
Similar Records
A comparison of texture results obtained using precession electron diffraction and neutron diffraction methods at diminishing length scales in ordered bimetallic nanolamellar composites
Bulk texture evolution of nanolamellar Zr–Nb composites processed via accumulative roll bonding
Interfacial orientation and misorientation relationships in nanolamellar Cu/Nb composites using transmission-electron-microscope-based orientation and phase mapping
Journal Article
·
Wed Aug 01 00:00:00 EDT 2012
· Scripta Materialia
·
OSTI ID:1067130
+8 more
Bulk texture evolution of nanolamellar Zr–Nb composites processed via accumulative roll bonding
Journal Article
·
Mon Apr 13 00:00:00 EDT 2015
· Acta Materialia
·
OSTI ID:1067130
+8 more
Interfacial orientation and misorientation relationships in nanolamellar Cu/Nb composites using transmission-electron-microscope-based orientation and phase mapping
Journal Article
·
· Acta Materialia
·
OSTI ID:1067130
+6 more