X-RAY ABSORPTION SPECTROSCOPY OF YB3+-DOPED OPTICAL FIBERS
Optical fibers doped with Ytterbium-3+ have become increasingly common in fiber lasers and amplifiers. Yb-doped fibers provide the capability to produce high power and short pulses at specific wavelengths, resulting in highly effective gain media. However, little is known about the local structure, distribution, and chemical coordination of Yb3+ in the fibers. This information is necessary to improve the manufacturing process and optical qualities of the fibers. Five fibers doped with Yb3+ were studied using Extended X-ray Absorption Fine Structure (EXAFS) spectroscopy and X-ray Absorption Near Edge Spectroscopy (XANES), in addition to Yb3+ mapping. The Yb3+ distribution in each fiber core was mapped with 2D and 1D intensity scans, which measured X-ray fluorescence over the scan areas. Two of the five fibers examined showed highly irregular Yb3+ distributions in the core center. In four of the five fibers Yb3+ was detected outside of the given fiber core dimensions, suggesting possible Yb3+ diffusion from the core, manufacturing error, or both. X-ray absorption spectroscopy (XAS) analysis has so far proven inconclusive, but did show that the fibers had differing EXAFS spectra. The Yb3+ distribution mapping proved highly useful, but additional modeling and examination of fiber preforms must be conducted to improve XAS analysis, which has been shown to have great potential for the study of similar optical fi bers.
- Research Organization:
- DOESC (USDOE Office of Science (SC) (United States))
- Sponsoring Organization:
- USDOE Office of Science (SC)
- OSTI ID:
- 1052086
- Journal Information:
- Journal of Undergraduate Research, Vol. 8
- Country of Publication:
- United States
- Language:
- English
Similar Records
XANES and EXAFS of dilute solutions of transition metals at XFELs
Local structure in LaMnO{sub 3} and CaMnO{sub 3} perovskites: A quantitative structural refinement of Mn K-edge XANES data