Dynamic material properties of refractory materials: Tantalum and tantalum/tungsten alloys
- Sandia National Labs., Albuquerque, NM (United States)
- Lawrence Livermore National Lab., CA (United States)
We have made a careful set of impact wave-profile measurements (16 profiles) on tantalum and tantalum-tungsten alloys at relatively low stresses (to 15 GPa). Alloys used were Ta{sub 97.5}W{sub 2.5} and Ta{sub 90}W{sub 10} (wt. %) with oxygen contents of 30--70 ppM. Information available from these experiments includes Hugoniot, elastic limits, loading fates, spall strength, unloading paths, reshock structure and specimen thickness effects. Hugoniot and spall properties are illustrated, and are consistent with expectations from earlier work. Modeling the tests with the Steinberg-Lund rate-dependent material model provides for an excellent match of the shape of the plastic wave, although the release wave is not well modeled. There is also a discrepancy between experiments and calculations regarding the relative timing of the elastic and plastic waves that may be due to texture effects.
- Research Organization:
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 104427
- Report Number(s):
- SAND-95-0802C; CONF-950846-13; ON: DE95016756
- Resource Relation:
- Conference: American Physical Society biennial conference on shock compression of condensed matter, Seattle, WA (United States), 13-18 Aug 1995; Other Information: PBD: [1995]
- Country of Publication:
- United States
- Language:
- English
Similar Records
Comparison of experimental shock-wave profiles for tungsten and computer simulations using a rate-dependent constitutive model
Compressive strength measurements in aluminum for shock compression over the stress range of 4-22 GPa