A simple method to ordered mesoporous carbons containing nickel nanoparticles
- ORNL
A series of ordered mesoporous carbons containing magnetic Ni nanoparticles (Ni-OMCs) with a variety of Ni loadings was made by a simple one-pot synthetic procedure through carbonization of phenolic resin-Pluronic block copolymer composites containing various amount of nickel nitrate. Such composite materials were characterized by N{sub 2} sorption, XRD, and STEM. Ni-OMCs exhibited high BET surface area, uniform pore size, and large pore volume without obvious pore blockage with a Ni loading as high as 15 wt%. Ni nanoparticles were crystalline with a face-center-cubic phase and observed mainly in the carbon matrix and on the outer surface as well. The average particle size of Ni nanoparticles was dependent on the preparation (carbonization) temperature and Ni loading; the higher the temperature was used and the more the Ni was incorporated, the larger the Ni nanoparticles were observed. One of the applications of Ni-OMCs was demonstrated as magnetically separable adsorbents.
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1043967
- Journal Information:
- ADSORPTION-JOURNAL OF THE INTERNATIONAL ADSORPTION SOCIETY, Vol. 15, Issue 2; ISSN 0929-5607
- Country of Publication:
- United States
- Language:
- English
Similar Records
Nitrogen-enriched ordered mesoporous carbons through direct pyrolysis in ammonia with enhanced capacitive performance
Nitrogen-enriched ordered mesoporous carbons through direct pyrolysis in ammonia with enhanced capacitive performance