Chemical solution deposition method of fabricating highly aligned MgO templates
- Knoxville, TN
- Los Alamos, NM
A superconducting article includes a substrate having an untextured metal surface; an untextured barrier layer of La.sub.2Zr.sub.2O.sub.7 or Gd.sub.2Zr.sub.2O.sub.7 supported by and in contact with the surface of the substrate; a biaxially textured buffer layer supported by the untextured barrier layer; and a biaxially textured superconducting layer supported by the biaxially textured buffer layer. Moreover, a method of forming a buffer layer on a metal substrate includes the steps of: providing a substrate having an untextured metal surface; coating the surface of the substrate with a barrier layer precursor; converting the precursor to an untextured barrier layer; and depositing a biaxially textured buffer layer above and supported by the untextured barrier layer.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-00OR22725
- Assignee:
- UT-Battelle, LLC (Oak Ridge, TN); The Regents of the University of California (Oakland, CA)
- Patent Number(s):
- 8,088,503
- Application Number:
- 12/363,035
- OSTI ID:
- 1035059
- Country of Publication:
- United States
- Language:
- English
Similar Records
Chemical Solution Derived Planarization Layers for Highly Aligned IBAD MgO Templates
Biaxially aligned template films fabricated by inclined-substrate deposition for YBCO-coated conductor applications.